Electronics Forum | Tue Nov 30 18:02:45 EST 2010 | flipit
62/36/2 is used often in thickfilm hybrid circuits where Pd/Ag conductors are used. The idea is that you saturate the joint with the 2% silver and thus help eliminate the leaching of the silver from the hybrid circuit pads or the component. We mix
Electronics Forum | Wed Aug 16 16:43:47 EDT 2000 | Steve Thomas
O.K., I give up. I am through trying to solder thermocouples on to 20 mil pitch QFPs. Whether it's my lousy technique (fairly likely), the wrong solder (Kester calls it thermocouple solder, and who am I to argue...it's a Sn10Pb88Ag2 alloy) or just
Electronics Forum | Thu Aug 21 21:05:39 EDT 2003 | Tom B
Dan, We, do alot of double reflow. Your right we typically see alot of the standards components, SOT's, SOIC's, Chip stuff. The largest we do with out adding epoxy is some 32pin PLCC's. We have several assemblies were were doing PLCC44's, Sockets
Electronics Forum | Fri Sep 17 03:55:45 EDT 1999 | Brian
| We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a reco
Electronics Forum | Fri Sep 17 06:01:12 EDT 1999 | Earl Moon
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re
Electronics Forum | Fri Sep 17 09:54:40 EDT 1999 | Brian
| | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a
Electronics Forum | Fri Sep 17 10:09:17 EDT 1999 | Earl Moon
| | | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However,
Electronics Forum | Fri Sep 17 15:01:05 EDT 1999 | Dave F
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re