Electronics Forum | Thu Jun 29 12:07:09 EDT 2017 | georgetruitt
HOW THICK IS THE BOARD? IS THERE A LOT OF COPPER IN THE BOARD? DOES YOUR CUSTOMERS PROVIDE HEAT RELIEF IN THE BOARDS BARREL DESIGN THERE NEEDS TO BE PLENTY OF ROOM FOR LEADFREE SOLDER TO FLOW, DID YOU CHECK YOUR PIN(LEAD)TO HOLE (BARREL) RATIO? N
Electronics Forum | Tue Feb 24 09:52:14 EST 2004 | davef
First, two points about hole / barrel fill are: * A filled hole is an excellent indicator of the optimum process and optimum quality PCB. * The study that showed that holes need not be filled was paid for by the US Army and performed by Lockheed in
Electronics Forum | Thu Aug 09 23:11:23 EDT 2001 | davef
Cheery disposition??? Would a few ;-) ;-) ;-) help? [Oh and look who is talking, the one planning the Mickie D gig after the traces on the this board start vaporizing with the fuseable link schtik.] Are you sure you're getting flux all the way up
Electronics Forum | Tue Jun 20 21:30:05 EDT 2006 | davef
The minimum vertical hole fill is defined as follows: Class 1: Not specified, with a 270-degree circumferential fillet and wetting on the secondary (solder source side) of lead and barrel, and a 75% coverage of the land area on the secondary side. Cl
Electronics Forum | Mon Jan 15 11:41:56 EST 2007 | davef
Questions are: * Does the component take solder when you dip it in the solder pot to test the solderability of the leads? * Can you get full barrel fill when wave soldering a bare board? * Is your flux reaching the top of the board through the hole b
Electronics Forum | Fri Oct 15 11:32:04 EDT 2010 | patrickbruneel
Inspecting for plating problems shouldn’t be part of incoming inspection. Your board manufacturer should have the appropriate process control. I shouldn’t have said barrel cracks but plating skips. Plating skips are caused by dull drills or a too hi
Electronics Forum | Tue Feb 02 10:12:50 EST 1999 | Justin Medernach
| Does anyone have any reliability data /concern on pressfit rework/repair - is there any qualified /characterized equipment /tools present in the industry? | What kind of effect does it have on barrel plating quality (1.5mil avg.) after 1 time rewor
Electronics Forum | Fri Sep 19 18:15:04 EDT 2003 | joeherz
Russ, I had arrived at basically the same specs here. Thanks for the effort. Regards.
Electronics Forum | Sat Aug 04 07:44:25 EDT 2007 | davef
Thermal cycle* * Requirements for and troubleshooting of poor barrel fill => Hole fill
Electronics Forum | Mon Oct 25 08:35:44 EDT 2010 | patrickbruneel
Thank you for the feed back. This is many times missing in the forum “how the problem got solved”. Patrick