Electronics Forum | Tue May 20 16:23:41 EDT 2008 | wintech
What is everyone using for BGA's ? For Lead Free Process, No-Clean or Water Wash solder past? Thanks, Steve
Electronics Forum | Wed Mar 20 13:54:56 EST 2002 | Aaron C
I am starting to use BGAs more and more in our process, which is using water soluble paste. Taking to the Paste Rep, he had pointed out that if you add Surfactant Packs to your inline water wash, that it would help get the water underneath the BGA pa
Electronics Forum | Fri May 23 09:37:14 EDT 2008 | llaerum
Water Soluable.
Electronics Forum | Fri Aug 16 09:59:49 EDT 2002 | dason_c
We baked the board first and print 2 mil water soluble paste at the BGA location and reflow. Wash and baked before the production run.
Electronics Forum | Thu Feb 10 18:53:04 EST 2000 | Russ
It is okay to use OA flux if you have a very robust cleaning process. lots of water and saponafier are good things. No-Clean is much safer when it comes to reliability. I personally like the Indium no-clean products. Russ
Electronics Forum | Wed Aug 04 16:46:40 EDT 2004 | davef
We assume this is different discussion that the discussion about "crystallized flux under BGA". Correct? Milky residue with water washing makes us think "noclean flux res that just got washed". We know what you said, but we can't help ourselves.
Electronics Forum | Tue Mar 30 22:30:06 EST 2004 | davef
Tony First, drying at 125*C for an hour is not going to do much drying. Heck, those boards are barely warm to the touch. Second, tell us about: * Pitch of your uBGA * Solder paste flux * Cleaning process and agents
Electronics Forum | Mon Apr 12 11:43:11 EDT 2004 | wgaffubar
Your wash unit should dry the boards well enough for you just take them and run them second pass within minutes of exiting the wash unit. We did it for years with no problem at all. If you must the hour at 125 will dry the wash water more than enough
Electronics Forum | Tue Apr 13 17:48:54 EDT 2004 | davef
Q1: Can anyone explain to me about the effect of their mixture. A1: What is their �mixture�? Q2: What enhancement does my BGA will have when using a WS paste flux with regards to corrosion, 25 years life cycle of the solder joint. A2: Tough to say