> What about designators? Using gerbers to program > a pnp machine was always a last resort to be done > only after much complaining and begging for > proper CAD data. Back in the day I used UniCAM to > program a mydata. After gett
Electronics Forum | Thu May 30 10:31:03 EDT 2002 | robbied
Hi Yannick. This is an issue that we are just recently getting into but here is some ifo that I have gathered so far. I have seen/ used 2 different rework machines. The one we have bought is a 'PACE TF2000' which was at the lower cost end of the mar
Electronics Forum | Tue Jun 16 15:00:12 EDT 1998 | Gary Simbulan
There are some common reason for capacitor cracking on my web page if you want to have a look. The document can be downloaded for your reference. | Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior
Electronics Forum | Mon Jun 08 15:29:17 EDT 1998 | Gary Simbulan
| Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. | First the caps. We stil
Electronics Forum | Tue Jun 16 15:01:58 EDT 1998 | Gary Simbulan
There are some common reason for capacitor cracking on my web page if you want to have a look. The document can be downloaded for your reference. | Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior
Electronics Forum | Mon Jun 08 14:52:16 EDT 1998 | Gary Simbulan
| Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. | First the caps. We stil
Electronics Forum | Mon Jun 12 17:32:17 EDT 2006 | flipit
Hi, A little off subject but I just finished a quick little experiment where I placed 0201 to 1206 and some ceramic resonators at specific distances off the scored edge. The distances from scored edge ranged from 0.025" on up at 0.025" increments.
Electronics Forum | Tue Feb 08 14:49:23 EST 2000 | Travis Slaughter
I have never tried this and wouldn�t really even want to consider it. Epoxy generally cures at around 160c in a fairly short amount of time, solder paste requires much more time and a peek temperature of about 210c or more in some cases. Curing you
Electronics Forum | Wed Nov 07 21:36:17 EST 2012 | davef
Multiple process and rework thermal cycles are brutal on boards and components. Improving reliability of products through reducing thermal stress ends-up being a major driver to the interest in lower MP LF solders. Binary LF solders require the addit
Electronics Forum | Tue Mar 23 07:35:42 EDT 2010 | jooh
Since I'm new to the forum I probably ask previously answered questions (that I have not found) but I would be grateful if someone could clarify this for me. I'm in R&D at a company where we design low volume (1k-10k) fairly complex PCBAs for our pr