You can most certainly use the same reflow oven for both leaded and lead-free pastes. Obviously your thermal profiles will be different, as the lead-free paste should have a higher reflow temp. As long as your oven has adequate exhaust and flux manag
Electronics Forum | Sat Jul 08 00:06:16 EDT 2000 | Edmund
Can any pls enlighten me what is the purpose of using DI water during washing of PCBA. If the board is not wash using DI water , what will happe? What is the range of resitivity reading should be. Rdgs...
Electronics Forum | Mon Dec 26 20:36:20 EST 2005 | davef
Look here to get started: http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=38261
Electronics Forum | Thu Aug 30 07:46:07 EDT 2007 | davef
Search the fine SMTnet Archives to find threads like: http://www.smtnet.com/Forums/Index.cfm?CFApp=1&Message_ID=51367
Electronics Forum | Tue Dec 27 07:22:44 EST 2005 | davef
It could be lots of things. You're not helping to narrow those alternatives. So, consider taking a sample to: * An analytical laboratory. * Teachers in the chemistry department at a local university. Kester recommends the following independent la
Electronics Forum | Mon Nov 13 11:31:10 EST 2000 | John Rep
I am having a problem with wetting on some feedthru wires. The problem seems to be contamination on the wires, due to the fact that the problem seems to be wire lot dependent. I have analysed it using SEM and come up with very little. Is there ano
Electronics Forum | Tue Jan 20 10:00:25 EST 2015 | TM
Hello We are currently cleaning stencils from both process (PbSn and lead free) in the same cleaning machine. A customer is concerned about cross contamination of lead between stencils. Is there any test kit or tool that you can suggest to test the
Electronics Forum | Thu Apr 12 09:12:19 EDT 2018 | san_jeev490
Hello, currently I am being getting solder pot contamination test form my supplier and results found okay to except. during the audit question was raised on historical data analysis, I request can some help me by sharing excel graphical template to
Electronics Forum | Mon Aug 09 11:34:25 EDT 2004 | Woodsmt
I am looking for data / info on how flux may contaminate the solder in a Wave. I have a customer who requires a no clean process. Our wave is equipped with 2 separate fluxing systems and I would like to use OA in one and the No Clean in the other. Th
Electronics Forum | Wed Jan 12 13:42:19 EST 2011 | dwonch
Hi All, I'm hoping there is a PCB expert or two hanging around. We're having some solderability issue on our boards. The finish is ENIG but it doesn't seem to be related to the finish process itself. We did SEM and EDX analysis and found aluminum an