Electronics Forum | Thu Nov 03 21:40:40 EST 2005 | davef
There maybe multiple drivers to your problems. * First, decreasing bond quality with time indicates a plating issue. What's the actual thickness of your gold and nickel on the pads? * Second, the no-sticks indicate contamination. If it's organic, p
Electronics Forum | Tue Apr 06 17:01:24 EDT 2004 | davef
It doesn't make sense that contamination would form on your gold pads after prebake of 150C for 3 hrs. The contamination must have been there prior to the bake. Your description makes us think of solder mask bleed. Tell us about: * Solder mask * S
Electronics Forum | Thu Nov 03 12:48:14 EST 2005 | Rosewood
We have some no sticks, but that is actually a good thing because we have NSD. During process control audits we found that pull strengths to the board dropped off. We build a military application that requires higher bond strenghts. Low pull streg
Electronics Forum | Mon Sep 09 15:38:02 EDT 2013 | arendonk
Hi, We are having issues aluminum wirebonding on ENEPIG plated PCB by a too low pull force and or having lifts (1% range). Could any body advice how to solve this problem? Is there a special wire bond grade required? How to best clean contaminant
Electronics Forum | Fri Nov 13 20:17:35 EST 1998 | Chuck Garth
| | I believe that gold fingers on my circuit boards are being | | contaminated and need to clean them with some chemical | | solution. Any recommendations. | | | Chuck: What is the type and source of your contamination? Dave F | We are using a s
Electronics Forum | Tue Jun 02 18:01:47 EDT 1998 | Earl Moon
| | | We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is no
Electronics Forum | Mon May 29 23:39:11 EDT 2006 | Faizal
Can anyone advice me on the effect of SN100C wave solder on SAC305 hasl board? I suppose the silver content on the hasl pcb would leech(contaminate) into solder pot.? Would it affect the surface bonding between copper pad and the solder.?
Electronics Forum | Wed Dec 14 20:17:48 EST 2016 | davef
As I understand, you are wire bond gold wire to gold pad, where the substrate has good bond strength, but the die does not. If bond quality is good, and then drops off rapidly, then it's probably something to do with contamination within the system
Electronics Forum | Tue Jan 30 20:38:32 EST 2007 | davef
NASA Internal Advisory: NASA-Issued Return to Flight Wristbands Contaminated with Silicone [snip] 10. PROBLEM DESCRIPTION: Recently we have been made aware of a silicone problem associated with the "Return to Flight" wristbands. These wristbands are
Electronics Forum | Wed Apr 07 22:15:31 EDT 2004 | davef
We're not familiar with the AUG5 from Taiyo. [It doesn't show on their US site.] Is it liquid photoimageable? Printed solder masks are more likely to bleed. But you wouldn't have any solderability with bleed. Your plating seems acceptable [if th