Electronics Forum | Wed Jun 05 21:33:12 EDT 2002 | davef
Tough to say based on what you have told us. Things to Determine are: * Is the heat at the solder connections that are not reflowing properly adequate? * Is the pad surface of the solder connections that are not reflowing properly solderable?
Electronics Forum | Fri Aug 24 09:29:08 EDT 2007 | jgrootkoerkamp
Solder balls with wave soldering can have different causes. The two most important are the solderresist and the flux. I have similar problems, after changes the flux type 90% off all solderballs are gone. KR, Joris Groot koerkamp
Electronics Forum | Tue Sep 29 11:49:02 EDT 2015 | spoiltforchoice
Typically - hand soldering as you are currently doing. Should your volume justify it you can invest in a selective soldering solution, these might take the form of a robotic arm that essentially replicates manual soldering or a solder jet similar to
Electronics Forum | Sat Oct 06 05:33:47 EDT 2001 | spchua
I had recently encounter the "black and grey" pads problems for the BGA pad after the convection re-flow. The pads shows in in "black and grey" color and a litter solder in it, and it happen in ramdom, when applied heat and solder on the "black and g
Electronics Forum | Tue Oct 22 17:23:35 EDT 2002 | Yannick
Hi, I wondering if someone know the anwser to that. I'm using a solder paste 63/37 and on the solder joint we have a tiny little layer or flux who is like crystalin. I try to play with my profile the get it off but I don't get much success. So D
Electronics Forum | Thu Jun 22 17:47:05 EDT 2006 | davef
First, we expect voiding in imm silver to be similar to ENIG. We expect more voiding in OSP than other common solderability protection. Second, choosing a solder paste, which does not contain resins and activators that decompose at higher temperatu
Electronics Forum | Fri Aug 24 11:03:15 EDT 2007 | hussman
I agree with Joris. But to add to his comment, the type of finish also has a direct affect to your wave solder process. Going from a gloss finish to a matte finish may help a lot. As for humidity affecting your wave - I doubt it. I use a water
Electronics Forum | Fri May 17 10:53:15 EDT 2013 | davef
ENEPIG or Imm Pd? Concerns about palladium as a solderability protection are: * Palladium is more difficult to process in fab than gold * Palladium solder alloys can be brittle, similar to gold, without proper soldering process and/or specification/
Electronics Forum | Tue Oct 12 10:24:50 EDT 1999 | Jose RG
Hi, We are in the way to evaluate different solder pastes, improve our solder paste incoming inspection steps, re-define our stencil requirements and the following questions are open. Two questions, 1- Is anybody using/requiring 1000 Kcps or more
Electronics Forum | Tue Jun 29 14:42:55 EDT 2004 | davef
You're correct, for every dumpster full of paper written about solder, there's a sentance written about fluxes. There's dribs and drabs about fluxes in most of the soldering books [ie, Manko, Klein-Wassink, Judd, Strauss, etc] and most of that is ve