Electronics Forum | Thu Jul 06 12:52:35 EDT 2006 | samir
..and he can put the flux in and keep it a secret too from his customer.. RSS profile on wave?? I never heard of a soak zone for wave preheat...you may be burning off your activator..hence, the beads. For wave preheat, your main goal is to ramp up
Electronics Forum | Mon Dec 17 13:58:54 EST 2007 | ck_the_flip
I made my own wave measuring device using KIC2000 system. KIC2000 has automatic wave detection, so now I have a profiler for both reflow ovens and wave solder. The delmat carrier only cost $500. A guy, Samir, from this forum gave me the idea, actu
Electronics Forum | Mon Jul 03 05:39:05 EDT 2006 | ronalds
Hi, I am experience problems while testing wave soldering SMT components that are glued on the solderside (lead free). Between de leads of SOx type IC's and SOT's develop a great deal of solder beads. I have been using a RSS temp.profile while spr
Electronics Forum | Tue Sep 02 22:03:03 EDT 2008 | davef
Try: * IPC-7530, Guidelines for Temperature Profiling for Mass Soldering (Reflow and Wave) http://portal.ipc.org/Purchase/ProductDetail.aspx?Product_code=3f5288fc-b386-db11-a4eb-005056875b22 * http://www.smtinfo.net/Db/_Reflow%20Soldering.html
Electronics Forum | Tue Feb 01 11:54:14 EST 2005 | TomA
Indy, I found the same findings as you. The claim is that the solder joint may actually look closer to a SnPb solder joint then the SAC alloys. I had commited to the SAC alloys at SMT before finding out about the SN100C alloy. I'm interested in what
Electronics Forum | Fri Nov 13 18:29:50 EST 2009 | luisreyes
really need help!! Our company is experiencing a change on the Quality system. one of the things that we are discovering is the amazing variation during the reflow oven and wave solder processes. this week we found that the team had not been performi
Electronics Forum | Thu Jan 27 16:43:15 EST 2005 | russ
Ther is a solder alloy out there that is supposed to allow lead free wave processing without having to upgrade pumps and such or increasing the pot temp (direct drop in). I have not used it nor do I plan on doing leadfree wave soldering but you may
Electronics Forum | Wed Jan 26 09:51:51 EST 2005 | jbrower
Sure, to be a true lead free enviroment all components need to be lead free or fall within the specifications of lead free as defined by the RoHS Directive. What I am doing is starting stage 1 of our journey. Layed out it looks some thing like this.
Electronics Forum | Tue Feb 01 12:52:19 EST 2005 | jbrower
Hi Tom, I did talk to Bob Gilbert about the sn100c. His comment is that it is a nickle stabalized alloy. Simplisticly, the tin and copper molecules would rather bond with the nickle. He also mentioned that with the SAC alloys, the manufactuers were
Electronics Forum | Wed May 12 16:31:25 EDT 2004 | Mark @ SolderStar
In answer to your questions. (1) pls can any body throw some light on the reflow profiling? Reflow profiling is the process of confirming that you PCB's that pass through your reflow oven are produced within specifications provided by solder paste