Electronics Forum | Wed Jan 04 17:06:20 EST 2006 | samir
All I can say about Alpha and their GOTT-DAMN website is THEY SUCK!! I refuse to register to view product literature... for that reason, Alpha Metals, you won't be looked at for my pb-free paste or bar solder evals.
Electronics Forum | Tue Apr 18 14:06:56 EDT 2006 | samir
Has anyone done a Wave Solder flux evaluation lately for no-clean/VOC-Free/lead-free? If so, please do share some feedback. Who're the best candidates out there, etc?
Electronics Forum | Tue Apr 18 18:34:57 EDT 2006 | George
Try 270WR flux from AIM solder. It showed very good results on our wave solder process. Let me know yours... Thanks, George
Electronics Forum | Thu Mar 22 14:01:08 EDT 2007 | JD
I actually already have this scope Gary. I was looking for something for PCB soldering assembly operations. Thanks for the suggestion though. I have had the new Mantis in here for an eval. Maybe ill bring it back in for another look now that Ive see
Electronics Forum | Tue Aug 23 15:27:38 EDT 2005 | Frank
I know this post is getting a bit old, but the Juki KE-2060 can do 0201 up to 74mm square (or up to 150mm long connectors) on their standard machine. You only need to purchase the 0201 nozzle and feeder. The machine is factory set to run 0201. And
Electronics Forum | Fri Jun 30 10:51:36 EDT 2006 | samir
Indium Pb paste has always been great but the flux tends to implode on the BGA's (despite many different profile strategies). The Indium Pb-Free is horrible...horrible, and have been kicked out of my lead-free eval. PS-I went to Moonman/Guru link a
Electronics Forum | Thu May 25 18:41:15 EDT 2006 | russ
How accurate is your placement machine? if it is accurate I would eval up to 25% off pad. the problem I might think you will have is errant paste or balls causing shorts if it doesn't coalesce completely. Bottom line is, if the board is good at th
Electronics Forum | Mon Feb 08 09:03:49 EST 2010 | woodsmt
Looking for methods for detecting BGA microcracks without cross sectioning. Currently evaluating a new package and will be putting together a thermal stress eval. We would like to perform intermediate inspections for cracks. Once all cycles are don
Electronics Forum | Tue Sep 22 16:09:41 EDT 1998 | Mike C
Hay Jim Don't get personal, I don't have time to go to the bathroom much less lift my horizons (or do you mean broaden). Anyway if it makes you feel better, next time I am going to purchase new equipment I will consider Panasert in the eval. I hav
Electronics Forum | Wed Mar 20 11:55:19 EST 2002 | slthomas
Interesting. Ours failed miserably. Of course we toss everything on the stencil at the end of a shift (they are instructed to let it run down to minimal volume on the stencil as they approach quitting time) so it's not an issue. We are more concer