Electronics Forum | Mon Jan 24 11:17:30 EST 2022 | jineshjpr
Hi, Mainly concentrate on 2 subjects: 1- Cleaning of Misprinted PCB (always use best neutraliser to remove paste from PCB), 2- Underneath Stencil Cleaning - Use good stencil cleaner (rather than IPA) to wipe your stencil. Because both the above said
Electronics Forum | Thu Sep 30 16:16:14 EDT 2010 | vetteboy86
Were doing double sided, and I'm told our PCB finish is tin silver. From a quick search I'm finding that for double sided assemblies we would be better off using ENIG.
Electronics Forum | Thu Jan 20 13:56:51 EST 2022 | stivais
For me it seems that the board is already assembled & soldered. Before assembling the board had been (poorly) washed (misprint perhaps) and the spots are just melted solder paste. Aren't those solder balls in the grooves between the pads and solder
Electronics Forum | Fri Jan 21 06:35:51 EST 2022 | stivais
"Manual washing" of a misprint board basically is smearing of printed solder paste all over the board. And trying to remove (wipe off) it afterwards. So for me it would not be any surprise that the solder paste ended up on the pads where it was not i
Electronics Forum | Fri Jan 28 13:49:48 EST 2022 | jseewald
That is correct. This looks like a board that was printed then wiped but not washed. Solder spheres left out on an unsolderable surface will just sit there like this or coalesce into solder balls. Nothing in the picture indicates an issue with the
Electronics Forum | Fri Jan 21 12:36:52 EST 2022 | stephendo
Like I said a lot of people don't tape the gold fingers the first time they run them. After that they make sure the fingers get taped up because solder gets places you don't think it does and once it touches gold, that gold is contaminated. How do y
Electronics Forum | Thu Jan 20 21:29:48 EST 2022 | stephendo
Copper gets etched in a photographic manner. ENIG is an additive process. Nickel gets added then gold gets added on top. Therefore it is not a matter of over etching. It is a matter of not enough gold added. The layer of gold ideally is as thin as po
Electronics Forum | Thu Sep 30 15:46:22 EDT 2010 | vetteboy86
Hi Folks, I'm looking for detailed information about the different composition of circuit board pads. We have been experiencing some issues with our solder, and I would like to know the differences between compositions. I do know that we ran a cust
Electronics Forum | Wed Oct 06 04:11:35 EDT 2010 | grahamcooper22
I've done minimal research to this point and > understand my issue with solder on the double > sided boards is due to oxidation that occures on > the unpopulated pads when the board makes its > first trip through the reflow oven. > > We did run
Electronics Forum | Thu Jan 14 04:45:16 EST 2016 | saimen
Hi There , Glad to contact with you , Here is Saimen in Tianweisheng , wish we will have a good cooperation in the furture if we have the honor . Our company is one of the largest custom-made PCB manufacturer in China. We can OEM,ODM,EMS single side
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
.gif)