Electronics Forum | Wed Jul 30 16:16:19 EDT 2003 | swagner
What is the industry standard for wave and selective solder PPM defect rate for a world class facility, any responses are appreciated.
Electronics Forum | Wed Jul 30 16:42:24 EDT 2003 | davef
here's a start http://www.thepdfshop.co.uk/ppm/asp/Monthly.asp
Electronics Forum | Fri Aug 01 00:30:04 EDT 2003 | caldon
Also Try: http://www.airliquide.com/en/business/industry/electronics/expertise/tech_papers.asp you can also search the airliquide site for "PPM" once in the electronics section Cal
Electronics Forum | Mon Jul 10 09:25:47 EDT 2006 | nodlac
Here is a nugget from the Data Sheet... Wave Soldering: Excess moisture on the PCB during soldering may lead to random solder balling and poor wetting of some solder joints. IT IS IMPORTANT that the flux solvent carrier (water) is fully evaporated a
Electronics Forum | Wed Jul 05 09:00:13 EDT 2006 | russ
Sounds like possibly too little preheat. Russ
Electronics Forum | Wed Jul 05 13:30:37 EDT 2006 | Chris Griffin
Likely causes of this are: -Preheat temp. too low -too much dross -uncured epoxy -PCB contamination ...also varify the solder flow over the wave is smooth.
Electronics Forum | Thu Jul 06 04:41:58 EDT 2006 | Rob
MF300S is quite an old flux, & a lot has happened since then on the flow solder front - are you sure it's designed for Lead free, or is it just a traditional flux that SHOULD work OK with Lead free?
Electronics Forum | Mon Jul 03 05:39:05 EDT 2006 | ronalds
Hi, I am experience problems while testing wave soldering SMT components that are glued on the solderside (lead free). Between de leads of SOx type IC's and SOT's develop a great deal of solder beads. I have been using a RSS temp.profile while spr
Electronics Forum | Wed Jul 05 10:13:02 EDT 2006 | jdengler
Is the flux rated for lead free? These higher temps will cause most lead rated fluxes to burn off prior to the wave. Jerry
Electronics Forum | Thu Jul 06 12:26:55 EDT 2006 | Chunks
Sounds like your flux to me. Since you cannot change the board or the machine, changing flux would be one question mark you could take away with a phone call and a sample. You will really be surprised how different fluxes can affect your final prod