Electronics Forum | Mon Feb 18 15:20:43 EST 2008 | kennyg
A PCBA contains a couple of parts that are not sealed and can't be water washed. We hand solder these with no-clean after everything else is water washed. The designer says the no-clean residue must be completely removed so that it will not affect
Electronics Forum | Mon Sep 28 09:35:28 EDT 1998 | Clive Heke
I have had some field failures returned recently, the boards had flux contamination under the components in a sensitive area, Nothing really visible until the component was removed, and the board had no evidence of rework of any type. Is it possib
Electronics Forum | Mon Mar 29 09:33:37 EST 1999 | Chrys Shea
| I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | What disadvantages are there when using this flux? | Do you have any contact details with
Electronics Forum | Tue Mar 30 08:11:27 EST 1999 | George Steele
| | I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | | What disadvantages are there when using this flux? | | Do you have any contact detail
Electronics Forum | Mon Apr 05 08:25:31 EDT 1999 | ADRIANO FERNANDES
| | | I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | | | What disadvantages are there when using this flux? | | | Do you have any contact
Electronics Forum | Wed Sep 05 14:53:45 EDT 2001 | Jeff Meier
We have customers that are requiring no flux residue left on boards after soldering of non-water washable parts. We currently use Multicore Crystal 502 No-Clean to solder parts that are not washable. Has anyone come up with a good way to remove this
Electronics Forum | Thu Sep 01 12:07:35 EDT 2016 | pavel_murtishev
Is there any field proven spray cleaning technique able to remove flux residues under OSRAM LEDs? Is it possible in principle? The problem is that OSRAM LEDs are low standoff ones and I absolutely have no idea how cleaning agent could get there. Mo
Electronics Forum | Thu Sep 06 10:34:21 EDT 2001 | Mike Konrad
Hi Jeff, Sean is correct. Although ultrasonic technology will work in post-reflow de-fluxing applications, you will receive concerns regarding ultrasonic �damage� to wire bonded components. Much has been written to combat this belief but the conce
Electronics Forum | Thu Sep 06 10:58:54 EDT 2001 | Steve
If I had to deal with this problem, I would switch to water soluble paste. It is a much more cost effective solution.
Electronics Forum | Fri Sep 07 21:43:40 EDT 2001 | mugen
Hi, We use IPA and Prozone, if IPA is so drastically detrimental, to the pcba's.....what suggested alternative, can you please recommend, as IPA replacement? Thanks.