Electronics Forum | Mon Jun 04 07:38:26 EDT 2001 | hussman
Ummm...Ok? Lumidor, The best thing to do is find out at which process this "wax" is occurring at. Targeting the process that just changed may be presumptuous on your part. Pick up the phone or make a visit. In either case, you're the customer a
Electronics Forum | Wed Dec 27 20:33:50 EST 2006 | greg york
water alone especially cold is not good enough, how do you check for hasl fluids when most residues left behind after improper cleaning are non ionic. Use 40C saponifier followed by heated rinse then cold rinse then DI rinse followed by dry.Nylon bru
Electronics Forum | Fri Sep 04 02:09:03 EDT 2009 | sachu_70
Hi Walter, Do you refer to a sprayfluxer operation? The problem seems to be a parameter setting issue. 1. Ensure the wide angle spray reaches PCB with optimum jet pressure. You could pass a glass plate to understand flux coverage and view Jet pressur
Electronics Forum | Fri Jun 01 12:07:53 EDT 2001 | medernach
No clean residues can range in appearance from brownish gunk that looks like tree sap (because it is in some instances) to almost no residue at all. Is this product exposed to a wave soldering process or SMT? I would guess it's a wave process if th
Electronics Forum | Fri Jun 01 16:22:35 EDT 2001 | davef
Your supplier�s approach to managing process change is TOTALLY UNACCEPTABLE!!!! Now, let me get the froth back in my mouth. How in the world do we know if the residues on these "no-clean" boards are compatible with your product? J-STD-001C, para 4
Electronics Forum | Wed Sep 05 14:53:45 EDT 2001 | Jeff Meier
We have customers that are requiring no flux residue left on boards after soldering of non-water washable parts. We currently use Multicore Crystal 502 No-Clean to solder parts that are not washable. Has anyone come up with a good way to remove this
Electronics Forum | Thu Jul 07 18:07:38 EDT 2005 | saragorcos
Ahh. sorry for the foul up - and thanks for stopping the spread of misinformation!! Sarag
Electronics Forum | Thu Jul 07 15:32:37 EDT 2005 | saragorcos
Hi Lloyd, Have you done any ionic analysis to find out what the flux residue is composed of? If you can eliminate the source residue, then your problem obviously should go away. Though tombstoning isn't known to be much of a functional problem it i
Electronics Forum | Mon Nov 01 19:52:47 EST 1999 | John
I have a thru-hole PCB that malfunctions when "no clean" flux is left on certain parts of the board. I have specified "the PCB shall have no flux residue". Our state side vendors (we have one offshore -they still use freon to clean) are complaining t
Electronics Forum | Thu Jul 14 09:26:30 EDT 2005 | saragorcos
Hello Lloyd, I have posted your picture in my photo library for all to see - you can find the page at http://www.residues.com/circuitree_pictures.html Hopefully that helps! Sara