Electronics Forum | Fri Jun 19 14:25:24 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | There has b
Electronics Forum | Fri Jun 19 13:40:25 EDT 1998 | Terry Burnette
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike There has been a
Electronics Forum | Wed Jun 24 16:23:29 EDT 1998 | Justin Medernach
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, Your concer
Electronics Forum | Thu Jun 25 09:53:04 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | Mike, | You
Electronics Forum | Fri Jun 19 10:03:46 EDT 1998 | Earl Moon
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, We and ind
Electronics Forum | Thu May 02 07:11:10 EDT 2002 | davef
They probably the same. Most likely someone is saying immersion gold [immersion Au] as a short hand for ENIG [ Electroless Nickel - Immersion Gold]. It is very uncommon to plate gold directly on copper, because gold and copper form a brittle interm
Electronics Forum | Sun Nov 08 15:27:25 EST 2015 | davef
Thinner: Flux thinner, NOT paint thinner We kept a spare stone in thinner in inventory. We cut PVC pipe to size, cap in one end, screw thread on the other, stone inside, filled with flux thinner and covered with a screw cap. I don't remember who we
Electronics Forum | Fri Jan 30 10:29:48 EST 2009 | petep
We have a potential new customer who has special PCB requirements. I do not know a lot of details at this point, but have several questions. One of their assemblies has within it , a MID, Solid foil layer, completely isolating one side of the PCB f
Electronics Forum | Wed Apr 13 13:40:27 EDT 2011 | jebs
Hi. the res/cap is mostly 805, solder paste will be led free and will only have a few fine pitch IC on each board. The boards will contain between 140 - 160 components and will run a production of 300 - 500 each day with only one or two different boa
Electronics Forum | Thu Aug 31 18:59:55 EDT 2000 | Brian W.
Our customers use OSP, HASL, immersion tin and immersion gold as board finishes. If I recommend a finish to the customer, it is one of the immersion finishes or OSP. Those finishes have the advantage of a flat surface to deposit paste. HASL has va