Electronics Forum | Thu Oct 02 01:47:57 EDT 2008 | myleb
I'm new to SMT. Now, i'm making program for SPI machine to inscpect for solder paste of SP60-MU. I think this is a very good printer but some times, my program shows only 50-60% of volume transfer; and the average height is very high: nearly 200 pct.
Electronics Forum | Thu Oct 02 17:00:44 EDT 2008 | davef
Is that accurate? If so, what are your aspect & area ratios? [Similar to the JerryS comment above.] * You say, � � and the average height is very high: nearly 200 pct.� => Our troop can make paste that height too. They snap the stencil-off a fast as
Electronics Forum | Thu Oct 02 12:22:26 EDT 2008 | JerryS
Hello Ok there is not much info here. What you have to mae sure of is several key factors. 1. Have you entered the correct stencil thickness. 2. Are you using the stencil gerber (not the paste layer) The paste layer is usually not adjusted for ap
Electronics Forum | Sat Apr 17 02:24:10 EDT 2004 | D. Sanders
What are the lengths/depth/height of these two machines? They will be used in-line with conveyors. Thanks, Doug
Electronics Forum | Thu Aug 20 15:03:59 EDT 2015 | saelectronics
We are in Glendale Heights IL.
Electronics Forum | Mon Mar 28 09:56:36 EST 2005 | n wolford
We have a granite table out on our production floor. We use the table along with metal parallel bars and a height gauge to measure component height. Some of these boards have components on them that may be ESD sensitive. Does anyone have experience w
Electronics Forum | Thu Jul 14 11:52:16 EDT 2005 | davef
Sure you can use SPC charting on the wave setup parameters to warn of impending problems. Examples of useful points of analysis are: * Dwell * Temperature * Pot analysis Certainly there's a range of other process controls that could be monitored.
Electronics Forum | Sun Aug 16 11:14:02 EDT 2015 | saelectronics
We also do maintenance on machines. Please let us know your location, we are in Glendale Heights IL. It would be a pleasure to help you. Our website is http://www.saelectronics.org e-mail-pcb@saelectronics.org
Electronics Forum | Fri Mar 03 14:40:22 EST 2006 | amol_kane
i think a more important issue here would be the reduction ratio. as LF solders have a higher surface tension, they do not flow as well as their leaded counterparts. therefore the stencil design may have to be changed (hence a new stencil) if the red
Electronics Forum | Tue Oct 12 10:24:50 EDT 1999 | Jose RG
Hi, We are in the way to evaluate different solder pastes, improve our solder paste incoming inspection steps, re-define our stencil requirements and the following questions are open. Two questions, 1- Is anybody using/requiring 1000 Kcps or more