Electronics Forum | Wed Feb 25 21:37:12 EST 2015 | dinhhuunam
Hi Bartel , 1.1 Profile Solution to Cold Soldering Cause for Cold soldering The peak temp of reflow is too low. The preheating temp is too high and it takes too long Solution Lower the preheating temp and increase the peak temp in the reflow zone
Electronics Forum | Fri Oct 08 10:08:48 EDT 1999 | Glenn Robertson
| | | | I have a board, 4 spacers needed to be soldered on the board | | | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first,
Electronics Forum | Tue Jun 22 17:14:41 EDT 1999 | Dennis Fall
I am looking to apply 10-15�m of a conductive material that will withstand 280�C. Our product consists of an alumina substrate sputtered with NiCr (2000�) and Copper (2000�) and 15-60 �m of electroplated copper (all metals patterned on the substrae)
Electronics Forum | Mon Dec 11 15:50:01 EST 2000 | externet
Hi ! Try fresh DRY solder paste... Keep solder paste in a sealed container until the moment of use. Humidity absorbed by the soldering paste becomes vapor violently at the moment of heating it , expelling the solder in form of balls everywhere.
Electronics Forum | Mon Dec 11 17:09:27 EST 2000 | Michael Parker
Get a profiler for your oven. To say "we are not sure" and "we think it might..." shows you are running with a WAG (Wild Ass Guess). Not a good place to be if you intend to produce anything reliable, with quality. Run your profile and verify that yo
Electronics Forum | Tue Dec 12 03:15:13 EST 2000 | Chris May
The profile that you should be using, hopefully, is detailed in the paste data sheet. Connect your thermocouples to various parts of the board, depending on layout, population etc; and then run some trials observing the profile on your oven monitor/
Electronics Forum | Tue Dec 12 17:54:04 EST 2000 | ralph
I've had this problem myself, though in using water soluables. But the process to eliminate it is still the same. There are three possible causes for this to occure. Too much humidity, to much solder, and too much heat. Are you leaving the paste
Electronics Forum | Wed Dec 13 19:40:38 EST 2000 | Jerry Wetzel, SME, EM/SME
Your profile must be precise, your stencil aperture sizes and shapes are very important, and the size of the pads on the boards should be very close to what the part manufacturer recommends. We had some trouble with hi-temp paste, and discovered tha
Electronics Forum | Wed Mar 16 20:12:12 EST 2005 | bkd
Does anyone knows any vendors that supplies jedec precondition tray that could stand up to 270�C peak reflow temperature.
Electronics Forum | Wed Jun 23 10:21:25 EDT 1999 | Chrys Shea
| I am looking to apply 10-15�m of a conductive material that will withstand 280�C. Our product consists of an alumina substrate sputtered with NiCr (2000�) and Copper (2000�) and 15-60 �m of electroplated copper (all metals patterned on the substra