Electronics Forum | Fri Dec 15 18:36:46 EST 2006 | Grant
Hi, I have noticed we are getting residue on our wave pcb's and it's worse with lead free, since we changed to the flux we are using. We are currently using Avantec VOC Free flux model Ecofree 303. It looks like it's made in Malaysia. Does anyone h
Electronics Forum | Mon Dec 18 23:24:50 EST 2006 | grantp
Hi, Yes, I would hate to resort to cleaning, but the product must be clean. We have been using palettes to keep most of the flux off the PCB, but there is still residue around the connectors. Does anyone suggest a good no clean flux to use with le
Electronics Forum | Tue Feb 19 09:41:26 EST 2008 | slthomas
ECD sells the MOLE, and they sell both the Oven Rider and the Wave Rider to accompany it. The thing is, you can profile both an oven and a wave machine without either if you're willing to just solder your thermocouples to a board. The nice thing ab
Electronics Forum | Tue Dec 19 16:26:24 EST 2006 | samir
Grant, Newer lead-free fluxes have 6%-10% solids content - more activator, therefore leave more "visible" residues. Old technology tin-lead fluxes got down to as low as around the 4%-6% range (I'm going off memory, so me might be wrong)... You'll
Electronics Forum | Thu Feb 16 12:41:50 EST 2006 | fredericksr
Hey folks, I was interested in any information that you might have on tombstone reduction when using a lead free solder and profile. Thanks for any input that you may have! -Russ #x
Electronics Forum | Fri Feb 17 09:02:21 EST 2006 | russ
proper pad geometries, accurate placement, and good reflow profile. Are you having problems right now?
Electronics Forum | Tue May 06 11:56:56 EDT 2008 | joeherz
We have a board that uses 0402x4 RNET packages that we are having a difficult time getting to solder consistently. Paste deposition is fine (using AIM WS353) and profile is dead-nuts. I'm starting to wonder if this is something that we're just goin
Electronics Forum | Tue Dec 13 17:41:04 EST 2011 | davef
A Study Of 0201’s And Tombstoning In Lead-Free Systems, Phase II Comparison Of Final Finishes And Solder Paste Formulations http://sheaengineering.com/Documents/APEX%2008%200201s%20and%20Tombstoning%20phase%202%20paper.pdf CONCLUSION The condition
Electronics Forum | Mon Feb 18 15:44:49 EST 2008 | ck_the_flip
Yup! All the major players out there - KIC, Datapaq, and ECD - are all capable of profiling both reflow and wave solder. check them out. www.kicthermal.com www.ecd.com www.datapaq.com