Electronics Forum | Mon Feb 07 12:42:25 EST 2000 | Brian E. Steelglove
Graham, Please describe the term OA? I have never heard of that acronym. Thanks, Brian E. Steelglove
Electronics Forum | Mon Feb 07 13:22:23 EST 2000 | Dave F
Brian: SMTnet has a "Terms & Definitions" section in the "Library." OA Flux. Flux, Organic Acid. A water soluble flux. Good luck Dave F
Electronics Forum | Thu Oct 24 10:05:59 EDT 2002 | Yannick
I don't know the name of the flux. but is a no-clean solder paste.
Electronics Forum | Mon Feb 07 13:20:03 EST 2000 | Dave F
Graham STOP!!! You can not be totally serious. A five year old cost model counts bean, and beans are beans. I have to know more about the calculation. If this bores some of your gear-heads, click on "return." � Help me with the terms: - "Ops cos
Electronics Forum | Wed Oct 23 08:40:20 EDT 2002 | davef
Yer not making this easy. What kind of flux? If no-clean flux, what controls are you using to assure you are: * Applying the correct amount of flux? * Properly activating the flux? If water washable flux, talk to us about your cleaning methods and
Electronics Forum | Tue Dec 19 10:08:10 EST 2006 | George
Grant, Why don't you try a water-base flux which is No-clean, VOC-free also? I have tried the 270WR flux from AIM with good results even on lead-free process. My $0.02, George
Electronics Forum | Mon Dec 18 14:36:09 EST 2006 | samir
Yikes!! In-line cleaning, to clean cosmetic and benign residues (from a NO-CLEAN) flux... You sure you can't switch fluxes? Another variable with residues is the solder mask. Depending on mask type (glossy, matte, semi-gloss, or semi-matte), will
Electronics Forum | Mon Sep 23 18:11:10 EDT 2002 | steveb
On an assembly reflowed in air saw the same thing: 0201's with a grainular solder joint, but 0402's and above with perfectly formed joints. Reflow profile all within acceptable tolerances. Reflowing in nitrogen solves this problem, but increases t
Electronics Forum | Wed Aug 21 10:26:08 EDT 2002 | stownsend
We are using OSP coated boards and no-clean solder paste. In a few instances, we are seeing increased distortion in an audio circuit. Has anybody seen or heard of surface insulation resistance (SIR) decreasing after reflow on OSP boards? Is it possib
Electronics Forum | Tue May 09 18:00:33 EDT 2006 | russ
in all actuality, you are both right. Alpha metals does have the toughest/hardest noclean residue that I have seen. When changing to no-clean FLUX you should run different probes. So back to square one. You're both right so who's gonna win?