Electronics Forum | Wed Mar 22 12:53:43 EST 2000 | David Spilker
Be careful if you use Ni/Au. The "black pad" phenomenum can be crippling. We moved from Ni/Au to OSP because of it. I also don't want to return to the lack of flatness of HASL.
Electronics Forum | Mon Jul 20 17:04:44 EDT 1998 | Richard Jackson
Can someone point me to where I can get a copy of the spec for these finishes. Thanks Richard Jackson richardj@tanisys.com Jackson_Richard@csi.com
Electronics Forum | Wed Jun 24 16:23:29 EDT 1998 | Justin Medernach
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, Your concer
Electronics Forum | Thu May 13 09:52:34 EDT 2021 | winston_one
Want to update this question a little, I know it appears few years ago, but I hope there is some updates... We have to assembly few samples of motherboards with this kind of finish (customer mistake during pcb order). Normally we can use leaded sold
Electronics Forum | Thu Jun 25 09:53:04 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | Mike, | You
Electronics Forum | Thu Aug 31 21:15:46 EDT 2000 | Dave F
From the SMTnet Library try: http://www.merix.com/resourcecntr/papers/osp.doc http://www.merix.com/resourcecntr/papers/hasl_alt.doc http://www.itm-smt.com/articles.html * "Organic Solderability Preservatives" * "OSPs - Better Living Through Modern Ch
Electronics Forum | Wed Aug 12 13:11:37 EDT 1998 | Tyler Posey
| Can someone point me to where I can get a copy of the spec for these | finishes. | Thanks | Richard Jackson | richardj@tanisys.com | Jackson_Richard@csi.com Richard We have also been looking into OSP's. Enthone-OMI is a source for anything you ne
Electronics Forum | Mon Nov 12 16:14:47 EST 2001 | davef
Yes!!! How can we assemble boards with 20 pitch when we allow 0.008� error to the master art? Excellent question!!! IPC-D-300G has nothing to do with assembler requirements. It is written by and for fabricators, so that they can be comfortable.
Electronics Forum | Fri Jun 19 10:03:46 EDT 1998 | Earl Moon
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, We and ind
Electronics Forum | Thu Aug 31 18:59:55 EDT 2000 | Brian W.
Our customers use OSP, HASL, immersion tin and immersion gold as board finishes. If I recommend a finish to the customer, it is one of the immersion finishes or OSP. Those finishes have the advantage of a flat surface to deposit paste. HASL has va