Electronics Forum | Fri Mar 03 14:40:22 EST 2006 | amol_kane
i think a more important issue here would be the reduction ratio. as LF solders have a higher surface tension, they do not flow as well as their leaded counterparts. therefore the stencil design may have to be changed (hence a new stencil) if the red
Electronics Forum | Thu Oct 02 12:22:26 EDT 2008 | JerryS
Hello Ok there is not much info here. What you have to mae sure of is several key factors. 1. Have you entered the correct stencil thickness. 2. Are you using the stencil gerber (not the paste layer) The paste layer is usually not adjusted for ap
Electronics Forum | Tue Jun 05 16:40:46 EDT 2001 | kerryn
Thanks Phil. However, my objective is to identify stencils that are not 100% clean prior to sending to inventory. I want to catch it before the solder paste has a chance to dry and harden in the apertures. Kerry
Electronics Forum | Mon Feb 19 11:36:39 EST 2001 | billschreiber
Hello Mark, I wish it were that simple so I could direct you to a particular manufacturer and stencil cleaner model. Unfortunately, there are several issues complicating the process of cleaning all these applications in one machine. First and fore
Electronics Forum | Tue Oct 12 10:24:50 EDT 1999 | Jose RG
Hi, We are in the way to evaluate different solder pastes, improve our solder paste incoming inspection steps, re-define our stencil requirements and the following questions are open. Two questions, 1- Is anybody using/requiring 1000 Kcps or more
Electronics Forum | Mon Sep 17 16:03:13 EDT 2001 | jschake
The results from an experiment comparing 27 different combinations of pad dimensions concluded that the pad design with 15 mil pad length, 12 mil pad width, and 9 mil pad separation produced the best assembly yields. A 5 mil thick laser cut stencil
Electronics Forum | Tue Nov 28 21:16:17 EST 2006 | davef
J Rose at EMPF says: The introduction of no-clean solder fluxes in electronics manufacturing has given rise to greater levels of solder balling simply because the opportunity to remove them in the wash process does not exist. They are typically cause
Electronics Forum | Mon Feb 19 11:25:07 EST 2001 | markt
I am currently cleaning solder paste and adhesive stencils and misprinted substrates manually by using IPA, chem wipes, Q-tips, etc. Can you recommend a machine and chemistry that will clean all these applications?
Electronics Forum | Tue Jun 28 00:11:30 EDT 2016 | ricoloverde
Hi, new to the forum here. First Post! Ive been using a Samsung sm482 for about 2 years and recently got the heads up that we will be getting a project soon with a BGA chip. Im wondering if anyone on here uses the SM482 for BGA and if so, can offer
Electronics Forum | Thu Oct 01 13:33:01 EDT 2015 | marlyn
Hey there fellow people with SMT > issues... What's the proper procedure for > soldering through-hole headers on the back-side > of the PCB (pins poking out on same side as SMT > parts)? ( Yes - I did the SMT side first and am > now faced with L