Electronics Forum | Tue Feb 08 14:49:23 EST 2000 | Travis Slaughter
I have never tried this and wouldn�t really even want to consider it. Epoxy generally cures at around 160c in a fairly short amount of time, solder paste requires much more time and a peek temperature of about 210c or more in some cases. Curing you
Electronics Forum | Thu Feb 10 16:00:31 EST 2000 | Travis Slaughter
I have had cases when it was necessary to run epoxy and paste at the same time. The only good reason I know of to even think about messing with going to this trouble is if the surface tension of the solder melting pulls the part out of alignment. T
Electronics Forum | Thu Aug 27 17:40:11 EDT 1998 | Earl Moon
| Does anyone have any experience they are willing to share on Ag epoxy used as a copper through hole plating replacement? Was CEM3 used? | What are the limitations? | Thanks, | Steve Steve, Hello again. Hope you guys (Intel) aren't going to do that
Electronics Forum | Thu Feb 12 21:30:45 EST 2004 | davef
Comments are: * We're amazed that you can thermocompression bond to epoxy. * Silver may be oxidizing during expoxy cure. * Klein Wassink talks about aging in THE BOOK [Soldering in Electronics: A Comprehensive Treatise on Soldering Technology for Sur
Electronics Forum | Wed Jul 05 13:30:37 EDT 2006 | Chris Griffin
Likely causes of this are: -Preheat temp. too low -too much dross -uncured epoxy -PCB contamination ...also varify the solder flow over the wave is smooth.
Electronics Forum | Wed Jul 29 12:58:35 EDT 2015 | pankyb1261
Is there anyone that makes a pick and place glue dot for surface mount chip components (B stage epoxy dot in a carrier tape)? Thanks, Rich
Electronics Forum | Tue Mar 18 11:53:58 EDT 2014 | sara_pcb
Our contract manufacturing agency have procured pcbs from approved vendor. After assembly we found solder mask separated from the PCB on the epoxy area as patches. The top side is intact. also over the pcb tracks, the mask got damaged. In what c
Electronics Forum | Mon Apr 12 19:28:26 EDT 1999 | Tom B
Netters, When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? 1. Kester 293 no clean 2. 2.1 C/s for 30s to 150 C 3. .5 - .7 C/s for 60s to 185 C 4. 1.5 C/s u
Electronics Forum | Fri Dec 17 13:23:15 EST 1999 | Chris
I have an underfill material which takes 6 hours to cure. It works great, better than any other underfill I have ever used. A vertical cure oven is too expensive. I am currently using batch style ovens and opening the oven door as additional produ
Electronics Forum | Thu Apr 21 11:43:03 EDT 2005 | davef
We understand the problem of trying to coat over RTV. We have seen the same problem with acrylic and urethane coatings not wanting to stick to RTV. Some acrylics seem to be worse than urethane. Since this is a new product, may be you could pot your