Electronics Forum | Thu Apr 28 08:08:46 EDT 2005 | Bruno Lalonde
Thank for your quick answer, waht to you mean by yammering, I'm sorry my english is not very good
Electronics Forum | Thu Apr 28 09:11:34 EDT 2005 | davef
Don't apologize. Your English is fine. * In Enlish look here: http://www.freesearch.co.uk/dictionary/yammering * In French, maybe: Parler � tort et � travers
Electronics Forum | Fri Jun 06 18:44:26 EDT 2003 | davef
No, no. It's koscher to have thermal planes. You just need to: * Work with your fabricator to keep the layup balanced. * Relieve the plane so that it doesn't cause assembly problems. While probably not directly for your part, it gives a starting p
Electronics Forum | Mon Mar 29 11:49:44 EST 2004 | gregoryyork
White residue, probably nothing to do with the flux but was more than likely mineral salts from resist cure problem that are only soluble in Mineral Acids. No residue is the best IF resist is good, if resist issue's use low solids Rosin No Clean and
Electronics Forum | Mon May 26 08:02:11 EDT 2003 | davef
Resistance: Tables of wire gauge often provide a resistance measure of some kind for each gauge. That way we can estimate the resistance of any length of wire we might be interested in. Calculating trace resistance is only slightly more complicated.
Electronics Forum | Tue Sep 14 13:36:11 EDT 1999 | Jeff Armato
I am looking to find a formula to calculate the resistance of circuit traces based on width
Electronics Forum | Fri Jun 18 08:19:12 EDT 1999 | Sergio Luiz Vito
There is a PCB with SMD components glued on bottomside. When I make tests for checking the resistance of glue the result is a break in the surface of PCB. How can I measure the surface resistance of PCB surface? How can I increase this resistance?
Electronics Forum | Thu Jan 19 16:25:03 EST 2006 | solderiron
Any metalurgists out there? I take the resistance value of a metal oxide substrate made of silver or gold or manganese. I then solder with 63/37 and the resistance changes but not dramatically. I then solder with Lead free SAC305 and the resistance c
Electronics Forum | Fri Jan 20 08:55:31 EST 2006 | patrickbruneel
Steve, How do you measure the resistance is it by probing the surface? Concerning the alloy there is a straightforward linear correlation between the tin content and the electrical conductivity of the alloy. The higher the tin content in the alloy,
Electronics Forum | Tue Aug 27 01:19:38 EDT 2002 | zolasteven
Hi, I have a few questions regarding printed circuit board. What is the difference between the solder pads and the solder resist or mask? What is the purpose for the solder resist? What color is it? When printing solder paste should the paste be