Electronics Forum | Thu Feb 15 10:48:34 EST 2007 | ck_the_flip
Is there anybody out there doing this scenario: SAC 305 Reflow & SN100C Wave and Selective Can the 2 alloys be mixed on 1 board, say, SAC 305 for SMT, and SN100C for thru-hole? Are 2 different rework chemistries needed, or can one use SN100c wire
Electronics Forum | Thu Oct 18 11:08:22 EDT 2012 | scottp
Since we follow IPC Class III, I've done experiments turning N2 on and off and measuring void level with both SnPb and SAC305 solder. In both cases there was a statistically significant, measurable increase in voids with N2, but it wasn't significan
Electronics Forum | Thu May 13 16:55:51 EDT 2021 | emeto
With Pb-Free HASL you can't use Pb process for sure as the melting point of tin is so much higher than the lead paste process. SAC305 is the most popular compound, unless your assembly requires something else for a specific reason.
Electronics Forum | Thu May 20 03:45:22 EDT 2021 | jineshjpr
SAC305 Will be the best choice with minimum TAL, Maximum Soak Solder Profile. Surely your solder Joint strength also will be more reliable & This can pass any kind of reliable Tests.
Electronics Forum | Thu Sep 23 08:08:12 EDT 2021 | SN
Hi. Anyone in this forum experienced the lead-free solder paste SAC305 and SAC405? What are the differences to expect for solder paste with SAC305 and SAC405? What is the effect of silver (Ag) alloy in solder paste? It was really appreciated if could
Electronics Forum | Thu Feb 15 14:10:59 EST 2007 | Cmiller
Russ is correct. We have been using SAC 305 for SMT and SN100C for wave and selective and repair for about a year. May switch to SN100C in SMT at some point if we can get some paste that wets better.
Electronics Forum | Tue Feb 20 16:42:31 EST 2007 | ratsalad
We have been using SAC 305 for reflow and Cobalt 995 (very similar to SN100C, only cheaper) for wave and rework for quite a while now with no issues that I'm aware of.
Electronics Forum | Fri Oct 01 01:25:55 EDT 2021 | sn
Thank you Djo for your sharing. By the way, do you know that which field/product will prefer to use SAC405 paste instead of SAC305 or lower Ag wt% alloy solder paste?
Electronics Forum | Tue Oct 05 12:46:02 EDT 2021 | emeto
From what I understand SAC305 and SAC405 are considered low silver content and have the better overall mechanical qualities compared to more silver or no silver.
Electronics Forum | Wed Dec 24 15:28:17 EST 2008 | edmentzer
We use SN100C for wave soldering and hand Lead free soldering and have had very good results. The wire cored solder for hand soldering flows good and makes very good solder joints. The SN100C in the wave solder machine also works very good. We use