Electronics Forum | Wed Mar 01 16:59:44 EST 2000 | Dave F
Robert: Expect a 0.033" raw ball to be within 0.022" of the pad, after reflow. To be clear, that�s not a matter of shrinking by 33%. The volume of solder on the pad is the same as the volume of solder in the raw ball. It�s just that the solder is
Electronics Forum | Wed Mar 01 10:46:26 EST 2000 | Robert Hartmann
Kelvin, Thanks for the help. The actual opening size is .440 mm, but I think what you said makes sense. After discussing with the customer, it looks like it is the height which matters, more than the diameter. We have learned that the height of t
Electronics Forum | Wed Mar 01 10:46:26 EST 2000 | Robert Hartmann
Kelvin, Thanks for the help. The actual opening size is .440 mm, but I think what you said makes sense. After discussing with the customer, it looks like it is the height which matters, more than the diameter. We have learned that the height of t
Electronics Forum | Wed Mar 01 16:58:03 EST 2000 | Dave F
Robert: On your balls: Solder suppliers make several "standard balls" and can advise you. On your cleaner: Recycling water / direct to drain? Most batch cleaner suppliers can advise you on recycling and filtering systems to keep you out of troub
Electronics Forum | Wed Mar 01 16:58:03 EST 2000 | Dave F
Robert: On your balls: Solder suppliers make several "standard balls" and can advise you. On your cleaner: Recycling water / direct to drain? Most batch cleaner suppliers can advise you on recycling and filtering systems to keep you out of troub
Electronics Forum | Tue Feb 29 21:53:46 EST 2000 | Kelvin Chow
Dear Robert, On PBGA assembly, BGA sphere shrinkage number depends to the following factors, a. BGA Sphere size (before reflow) b. Solder mask opening diameter As far as I know, no formular has been established yet. Most of my friends just collect
Electronics Forum | Tue Feb 29 21:53:46 EST 2000 | Kelvin Chow
Dear Robert, On PBGA assembly, BGA sphere shrinkage number depends to the following factors, a. BGA Sphere size (before reflow) b. Solder mask opening diameter As far as I know, no formular has been established yet. Most of my friends just collect
Electronics Forum | Wed Nov 17 00:59:33 EST 1999 | Gyver
Hello all, Recently we changed the vendor of flux. However, we would like to know in detail about how to qualify the new flux. Are there any procedures or standards to follow? Please help us to solve this problem by providing your knowledge and exper
Electronics Forum | Wed Jan 26 20:52:06 EST 2005 | Chua
Hi, I'm going to evalute new solder paste and flux for wave-solder. Appreciate you could advise what are the things need to look out during the evalution. Any recommend step or proper way of doing solder paste and flux evalution. Appreciate your he
Electronics Forum | Thu Jan 27 11:23:45 EST 2005 | russ
Well first off I wouldn't evaluate paste for a wave process. I would use solder bar instead. Flux - top side fillets and no shorting on the solder side, does it clean well after processing if using water soluble flux. How wide is the process win