Electronics Forum | Sun Feb 23 14:32:42 EST 2003 | davef
Sources of sulphur in PCB fabrication are: * Some locales have high H2S concentrations in the air. * Metal etching steps that use sulfuric acid or a sulfonated buffering compound may result in sulfate residues. * Sulfates can come from contact with
Electronics Forum | Thu Feb 09 20:12:51 EST 2017 | imarkl
Any advise about dewetting defect occurrence during 2nd pass reflow. Commonality on affected PCB having water marks near affected pad(s). Elemental composition found on affected pads without solder paste are Silicon and Sulfur. As well as in pad with
Electronics Forum | Tue Nov 29 17:18:26 EST 2022 | davef
Yes, electronics manufacturing is a volume producer of cardboard waste. If the components are ESD-critical, cardboard and most plastics are not ESD safe. Static charges can be generated on these materials during handling by the friction of dissimila
Electronics Forum | Wed Feb 21 21:28:24 EST 2001 | davef
I don't know where sulfur would get into your resistor supplier's process. Your processes are more likely candidates.
Electronics Forum | Thu Jan 17 14:52:17 EST 2008 | gnath
All, Can someone help find a source for purchasing interleaving/packaging paper for Immersion Silver boards (sulfur free + ph neutral ..). Thank you!
Electronics Forum | Sun Sep 21 10:55:52 EDT 2008 | vladig
As long as the surface is solderable, you should be fine. Silver tarnish a well0-known thing. Make sure, though, there is no sulfur (S) "around". Regards, Vlad
Electronics Forum | Tue Jan 26 12:25:44 EST 2010 | blnorman
You can try a 5% solution of sulfuric acid. It's used to clean copper foils to IPC-TM-650 method 2.3.15 prior to testing for purity.
Electronics Forum | Wed Nov 29 21:04:32 EST 2017 | davef
Yes, "corrosion" should be on your buyers spec for ESD mats. ESD mats are another one of those sneaky little gotcha things, where it's easy to think that all blue mats are the same. Kapon tape is another one where you can't purchase strictly based
Electronics Forum | Thu Jul 26 23:52:24 EDT 2007 | gioblast
HI..anyone who can give me a link to enlighten me on this plating for pb-free..Most people say this is the same? ARe they really? or different in process?? ..Any info on best storage for this plating? I have read all those stuff like avoiding sulfuri
Electronics Forum | Wed Aug 27 18:28:29 EDT 2008 | blnorman
We have an immersion silver board that has a brown discoloration after processing. It's not flux residue, that normally doesn't cause this condition. Elemental analysis shows less than 1% sulfur, and I thought silver sulfide is more a black color.