Electronics Forum | Wed Apr 11 19:32:39 EDT 2001 | Adam
I'm trying to find information/articles describing the effects of temp and humidity on solder paste. Just recently we have gone through a change outside temperature and humdidty and have notice solderabilty problems with smt boards.
Electronics Forum | Wed Apr 11 22:05:58 EDT 2001 | davef
OA pastes are more hydroscopic than NC pastes. Hydroscopic. The capacity of a material to absorb and retain moisture from the ambient air. Sometimes this is compounded if you remove paste from the frig and let it warm to room temperature, because
Electronics Forum | Wed Dec 17 18:56:02 EST 2003 | Chandler
Kev, You seem to have a very good knowledge of your process and can convey it clearly and precisely. My advise to you is to dis-regard the BS most of these guys churn out and follow your own gut. They will ask a s**t load of irrelevant Q's in some fu
Electronics Forum | Tue Oct 06 14:29:14 EDT 2015 | cadco
Update 6 Oct 15: We have completely re-configured the oven PID boards such that everything is now visible on the oven by the s/w and all is now OK since the "Machine"card is now recognized. We have just one additional procedure to do and that is to
Electronics Forum | Tue Apr 24 21:00:58 EDT 2018 | marlonbc
Hi All, Would just like to course through this concern on a product that we are contracted to assemble. It is mainly used for an automatic hand sanitizer dispensing product. By design there is a restrictive value of current that it needs to dissipat
Electronics Forum | Wed Jul 07 13:43:06 EDT 2004 | microniks
Thank you for helping finding a direction for my answer. I found interesting things on fluxes at this site: http://www.smtinfo.net/docs/Electronic%20Production/25.htm Due to the lack of precise and concise information on the subject, I think I will w
Electronics Forum | Wed Sep 18 14:12:40 EDT 2013 | pjchonis
Hello Bachman. SAC305 is the most common lead-free solder alloy, not only for wave soldering but also selective. Most of our selective customers (especially automotive) are using SAC305. What is more important than the alloy to consider is the flux
Electronics Forum | Fri Dec 16 18:37:10 EST 2005 | mdemos1
Hi. I am trying to understand Tg and how it relates to reflow. With the higher temperatures of lead free, we have been looking toward laminates with a Tg of 180 instead of the current 140. My question is a little more general. In either lead free
Electronics Forum | Thu Jul 14 11:52:16 EDT 2005 | davef
Sure you can use SPC charting on the wave setup parameters to warn of impending problems. Examples of useful points of analysis are: * Dwell * Temperature * Pot analysis Certainly there's a range of other process controls that could be monitored.
Electronics Forum | Thu Jul 27 21:34:41 EDT 2000 | Dave F
Gary: That's curious. Tell us more about your process steps, temperature profiles, paste, warping of the board without the PIH processing, components, etc
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830