DO YOU KNOW? WHAT KIND OF SOLDER PASTE IS BETTER IN ORDER TO AVOID THE TOMBSTONE DEFECT IN SMT PROCESS.
Electronics Forum | Sun Apr 13 19:57:51 EDT 2003 | Thomas
I saw some specifications on the Tamura RMA-012 FP stating that it counters tombstoning...hope it helps you problem...
Electronics Forum | Sun May 04 22:10:20 EDT 2003 | Thomas
Did u ever try a anti-tombstone solder paste to try to eliminate this problem ??
Electronics Forum | Wed May 07 09:24:33 EDT 2003 | davef
Kris The majority of our tombstoning in very small passive SMT is caused by imperfections in end-cap solderability protection plating.
Electronics Forum | Thu Jul 10 12:52:41 EDT 2003 | Terry Saunders
ALL, WE ARE HAVING TOMBSTONING ISSUES WITH LED'S -ANY HELP OUT THERE. PLEASE ADVISE. TERRY SAUNDERS.
Electronics Forum | Thu Jul 10 15:04:02 EDT 2003 | russ
Search the archives. There is a ton of tombstone discussion in there. Russ
Electronics Forum | Fri Jul 22 07:21:14 EDT 2005 | Mark
Try using Cobar`s anti-tombstone alloy.
Electronics Forum | Thu Jan 19 07:58:50 EST 2006 | chunks
Finny dat Darnel. Guess this proves that jerks can cause tombstoning.
Electronics Forum | Mon May 05 18:48:23 EDT 2003 | Kris
Hi, It is expected that lead-free will have reduced tomstoning. As it has a higher surface tension and does not wet as well as the tinlead paste it exibit lower tombstoning. Addiotnaly commercialy available lead-free alloys may not be true eutectic
Electronics Forum | Fri Jul 30 00:21:01 EDT 2004 | Jet
Hi, Very interesting article on tombstone issue, i'm facing tombstone issue for 0805 IDC component, i've redesign the stencil aperture and change to lead free paste, the tombstone is reducing but not fully eliminated, however there is a problem i fa