Electronics Forum | Mon Jul 19 11:11:18 EDT 1999 | Wolfgang Busko
| Perhaps a little hard to find but is there anyone who uses a vapor phase process to solder populated card with BGAs. I am interested in the success rate of such a process. It is obvious that the throughput is reduce vs a convection oven but still t
Electronics Forum | Mon Jul 19 11:50:47 EDT 1999 | Mario
| | Hi, SMTASSY | | that�s what we do, soldering our double-sided-finepitch-BGA-and all-the-other-stuff-boards in vapourphase because it�s the only thing we have. | First, we do not do real series produktion, only prototyping up to sometimes 20 uni
Electronics Forum | Mon Jul 19 12:37:15 EDT 1999 | Wolfgang Busko
| | | | | Hi, SMTASSY | | | | that�s what we do, soldering our double-sided-finepitch-BGA-and all-the-other-stuff-boards in vapourphase because it�s the only thing we have. | | First, we do not do real series produktion, only prototyping up to som
Electronics Forum | Tue Jul 20 05:29:14 EDT 1999 | Wolfgang Busko
| | | | | | | | Hi, SMTASSY | | | | | | that�s what we do, soldering our double-sided-finepitch-BGA-and all-the-other-stuff-boards in vapourphase because it�s the only thing we have. | | | First, we do not do real series produktion, only prototypi
Electronics Forum | Wed Mar 12 15:26:46 EDT 2014 | dan_ems
Hello, in my SMT process I have some problems with the solderability (look like dewetting) on a PCB with finish HASL Lead Free with a composition that is melt at 230 degree Celsius. My oven is with vapor phase and the peak temperature is 230 degre
Electronics Forum | Thu Mar 13 14:12:31 EDT 2014 | davef
You're creating a new alloy on the surface of your board. The alloy will have a melting point determined by the constituent metals of the alloy. Your alloy consists of: * Lead-free HASL solderability protection on the board * Lead-free solder paste *
Electronics Forum | Sat Mar 06 21:24:31 EST 2004 | Bryan
Hi, everyone knows that we will soon phase into Lead free process.would it neccessary to waste so much money for such a lead content monitor? Bryan
Electronics Forum | Sat Mar 06 22:26:34 EST 2004 | Ken
I think it is a good idea to "waste" money on this analysis. Especially if you phase in a SAC wave alloy. Silver is not toxicity free....and lead free waves can dross 3 to 5 times faster than SnPb alloys. This produces a greater potential for airb
Electronics Forum | Thu Dec 22 15:36:03 EST 2005 | CC
In general two step temperature reflow process requires minimum 40 deg C delta to be sucessful. We are not using vapor phase soldering but we have similar situation when we change to SAC lead free solder for PCB component population and secondary swe