Electronics Forum | Mon Jun 26 08:08:32 EDT 2006 | davef
It does make you think the immersion coating is causing the voiding, doesn't it? We never have seen that.
Electronics Forum | Wed Jun 28 16:16:09 EDT 2006 | Gman
Good article. Would EDX analysis of the cross-section at the void joints be a good method to determine any plating contamination or solder mask issues?
Electronics Forum | Thu Nov 01 10:57:34 EDT 2012 | kris1128
Has anyone heard whether the elevation of a plant can effect solder joint formation? One plant at sea level, one at 7,000 feet elevation... same equipment and profiles, big voiding defects at higher elevation. I did a search and found no similar post
Electronics Forum | Sun Mar 01 15:52:13 EST 1998 | Earl Moon
| From several months I am investigation about the VOIDS PERSENCE and his important as reliability. | One question now is : | It is possible that on the BGA components the voids are already present into the balls, before the mounting on the pcb ? | I
Electronics Forum | Thu Jun 22 07:15:37 EDT 2006 | amol_kane
do you mean microvoids or macrovoids??
Electronics Forum | Tue Jun 27 12:12:05 EDT 2006 | GMan
Yes it does seem like a plating issue and analysis is being done. Thank you for your inputs.
Electronics Forum | Wed Jun 28 02:29:48 EDT 2006 | Loco
Wow, great article there mike! Thanks for digging it up for us! Kind regards, Loco.
Electronics Forum | Mon Jun 26 23:33:20 EDT 2006 | KEN
We saw this condition over 3 years ago. It sometimes is called "champagne bubbles". The intemetalic formation is interrupted due to the micro voiding reducing mechanical strength. I discovered this on lead free test vehicles for a major computer
Electronics Forum | Tue Feb 08 12:36:28 EST 2000 | Charlie
I'm looking for information from both those who do cure glue and reflow past with the same profile and those who have tried and decided against it. What were the problem? What are the limitations?
Electronics Forum | Wed Jan 03 15:11:09 EST 2007 | kennyg
Is it acceptable to apply an acrylic conformal coat, cure and then apply a silicone RTV on top (for staking tall components)? Should there be a concern with the bond between the acrylic and the RTV?