Electronics Forum | Mon Dec 17 02:08:21 EST 2007 | mun4o
Hi, I have a lot of solder bridge in our wave soldering process.We use SACX0307 and Surf 11 flux.the SW mashine is Vitronics delta 6622.Itry to change flux and termoprofile but results is not god.Can you halp me - recommend me some flux or other adv
Electronics Forum | Mon Dec 17 15:41:15 EST 2007 | shrek
Ha-ha-ha-ha-ha,me lad. Wave solder is like an onion, it's got many many layers. Kind of like me-self. I'm a big ogre with many complex layers. At any rate i like the other colleague with his adverstising trigger finger. by golly, me chap, he's a
Electronics Forum | Mon Jul 03 05:39:05 EDT 2006 | ronalds
Hi, I am experience problems while testing wave soldering SMT components that are glued on the solderside (lead free). Between de leads of SOx type IC's and SOT's develop a great deal of solder beads. I have been using a RSS temp.profile while spr
Electronics Forum | Mon Dec 17 10:46:04 EST 2007 | realchunks
First of all, more info is needed. Solder shorts can be caused by much more than flux. Is the solder short always in the same spot or all over the place? More detail please.
Electronics Forum | Mon Dec 17 15:11:35 EST 2007 | chef
Blew chunks - thanx for thinking outside the box. Of course there's two sides to every story. Just last week I had a new operator "splash" a couple of boards. Top solder was great, it was all one big solder bridge. Come to find out, the operator forg
Electronics Forum | Thu Jul 06 04:41:58 EDT 2006 | Rob
MF300S is quite an old flux, & a lot has happened since then on the flow solder front - are you sure it's designed for Lead free, or is it just a traditional flux that SHOULD work OK with Lead free?
Electronics Forum | Thu Jul 06 12:26:55 EDT 2006 | Chunks
Sounds like your flux to me. Since you cannot change the board or the machine, changing flux would be one question mark you could take away with a phone call and a sample. You will really be surprised how different fluxes can affect your final prod
Electronics Forum | Mon Jul 10 07:46:51 EDT 2006 | ronalds
You are right, RSS profile is not the correct description. I am using a profile which heats up quickly to let the flux spread. Next linear up to activate the flux and prevent thermoshock. My experience is however, that small changes in this profile
Electronics Forum | Mon Dec 17 11:55:08 EST 2007 | chef
I recently had the same problems, solder bridges on every thing I made, different customers boards, etc. I wave with no-clean flux. As I sorted out problems (pin holes, blow holes, splatter, etc.) I found a lot of variable factors. I changed flux,
Electronics Forum | Mon Dec 17 19:01:45 EST 2007 | bbarton
As someone with a LOT of experience with the "low cost" alternative alloys, primarily SACX, I have one simple question....Are these shorts a new phenomena? WAS your process in control, and all of a sudden it's not? If the answer is YES, take a look a