Electronics Forum | Tue Dec 27 10:00:19 EST 2005 | sparrow
Hello, does anybody have experience in thermosonic gold wire bonding to electroless nickel/immersion gold?? regards, Sergey
Electronics Forum | Sun May 26 10:21:46 EDT 2002 | V.RAMANAND KINI
We buy PCBs for aluminium wire bonding. Our PCBs have 0.25 mm square pads for bonding and 0.10 or 0.15 mm gap between circuit traces/tracks. We do not have any problem. Our vendor gives 9 microns of Nickel and 0.03 microns of gold.
Electronics Forum | Wed Dec 28 21:18:12 EST 2005 | davef
You don't TS bond gold wire to nickel [of ENIG] for the same reason that you don't TS bond gold wire to hard gold. [Nickel or maybe cobalt is used to harden soft gold.] Together nickel and gold produce unreliable bonds. Look here: * http://www.smta.
Electronics Forum | Tue Dec 27 14:51:49 EST 2005 | davef
What's the issue and situation?
Electronics Forum | Thu Dec 29 03:57:16 EST 2005 | sparrow
Hello Chris, To be honest, it's hard to believe you could not bond to ENIG at all. Yes, the gold layer is thin and hard, but it just narrows the process window and does not make the bonding impossible. I say this, because we have been using TS gold w
Electronics Forum | Fri Jan 20 10:27:22 EST 2006 | sparrow
Hello David, No, the capillary does not scrub through the gold layer. At least, we have never seen it. We replace the capillary after approx. 200k bonds. Regards, Sergey
Electronics Forum | Sun Jan 22 20:45:24 EST 2006 | yihui
Hello Sergey, thanks for your input. The capillary i'm using seems to pick up material from the bond surface fairly quickly. Can't think of a solution at the moment. regards, david.
Electronics Forum | Mon Mar 03 10:38:28 EST 2003 | davef
Electroplated nickel and electroplated gold is the more �traditional� finish for aluminum wire bonding. That surface was an extension of gold thermosonic wire bonding that requires a thick [50 thou min] gold surface. For years fabricators recommend
Electronics Forum | Fri Jan 20 02:34:16 EST 2006 | yihui
Hi, i'm david, new to this forum. Came across your posting about using a delvotec bonder to TS bond to a ENIG pad. Given that the immersion gold layer is thin, does the capillary scrub through the gold layer to expose the underlying nickel? Does your
Electronics Forum | Wed Dec 28 16:03:53 EST 2005 | Chris
I have lots of experience with thermosonic gold ball bonding. You can read the literature and you will probably find some papers that say you can do it. I have never been able to do it. We gold ball bond all day long with little problems at all bu