Electronics Forum | Wed Jul 02 07:00:56 EDT 2003 | davef
Title : SOLDER JOINT RELIABILITY OF Sn-Ag-Cu BGA COMPONENTS ATTACHED WITH EUTECTIC Pb-Sn SOLDER PASTE Author : Fay Hua et al. Author Company : Intel Corporation Date : 01/01/2003 Source : Journal Of Surface Mount Technology, Volume 16-
Electronics Forum | Mon Jan 26 13:13:07 EST 2009 | rgduval
We've had this same problem with the solder wicking to the component terminations. However, in our case, we did not see the pads turning a silver-white color...rather, they exhibited a tarnishing/darkening of the gold. We determined that we had som
Electronics Forum | Mon Mar 30 11:39:46 EDT 2009 | rgduval
Is this a sample board that you ran without components? If so, I'd get it back to your board house, and ask them to explain to you what's happening. We never did get to a satisfactory root cause on our issue (at least, satisfactory to me). It seem
Electronics Forum | Fri Jan 06 00:03:10 EST 2023 | SMTA-64419298
Hello Evtimov, sorry...just saw post as I was looking through list...a bit late. I don't know if you ever got your answer. IPC-4552A covers EniG finishes and suggested shelf life. I've referred to these doc's quite a bit. Good spec's ! Yes, I beli
Electronics Forum | Thu Aug 31 09:53:56 EDT 2017 | mgsmtnet1210
Thank you Amalia for your reply but we are not looking any metals for pcb, we are looking specially Tin plating solution for plating purpose. If you do carry this please give your contact info. Regards, Hetal
Electronics Forum | Tue Dec 13 14:55:12 EST 2005 | muse95
Your response is from the point of view of using a Bismuth solder with Pb plated leads. Samir's point of view is from Bismuth in the plating on the leads being used with a Pb solder. There is a very large difference in the amount of Bi that will en
Electronics Forum | Mon Feb 27 06:42:37 EST 2006 | Slaine
What are the long term issues with high tin content solders on parts plated with silver over copper? Is it possible that the silver will be absorbed by the solder then over a long period of time the tin will react with the copper causing it to part
Electronics Forum | Thu Aug 03 07:47:38 EDT 2017 | mgsmtnet1210
Hello Everyone, Does any one know supplier of Immersion Tin plating solution in North America? Thank you in advance.
Electronics Forum | Thu Aug 03 12:51:07 EDT 2017 | mgsmtnet1210
Thank you so much.
Electronics Forum | Tue Feb 01 12:00:01 EST 2000 | K. Ckak
Hi Folks, I am looking for some info. and possibly a source on measuring inprocess copper plating thickness for Flex PCB manufacturing facilities. I have tried XRF, E-Current method but the supplier told us that it wont work with Flex material - th