Electronics Forum | Mon Jun 14 09:16:58 EDT 1999 | Adam Pratt
| | | | | Hello all! | | | | | Recently we got a problem about the Funtional test. Some boards passed tests by using the auto-fixture(vacuum), but failed by using manual test fixture(need to plug CPU, DIMM etc.). The error symptom is no picture. We d
Electronics Forum | Sat May 30 08:24:09 EDT 1998 | Dave F
| | | | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not locali
Electronics Forum | Sat May 30 12:51:29 EDT 1998 | Earl Moon
| | | | | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not loca
Electronics Forum | Wed Apr 04 08:57:13 EDT 2001 | Cal
IPC-TM-650 is a works well. Ionic conductivity is a good rule of thumb but I prefer ION Chromatography this will help determine the residues left behind from the fab process. There are a bunch of ways to determine solderabiltiy- Wet Balance and SERA
Electronics Forum | Fri Jul 20 17:09:10 EDT 2001 | davef
Circuits Assembly magazine 09/99 "Defluxing with Ultrasonics" by Les Hymes. [There's more but I can't find it right now. I'll add to this as I find the junk, er very nice stuff.] J-STD-001C states that its OK to use ultrasonics for cleaning so lon
Electronics Forum | Sat Jun 19 08:37:25 EDT 1999 | Dave F
| There is a PCB with SMD components glued on bottomside. When I make tests for checking the resistance of glue the result is a break in the surface of PCB. | | How can I measure the surface resistance of PCB surface? | How can I increase this resis
Electronics Forum | Wed Jun 16 14:14:07 EDT 1999 | Dave F
| Hello, | I am looking for the surface resistivity and volume resistivity of standard fr4 as a function of temperature and /or humidity . can any one help? | Frank: Sorry I'm so late getting back to you. 1 Use either ASTM D5109-94 or IPC-TM-6
Electronics Forum | Fri Jun 18 03:31:38 EDT 1999 | Frank
| | Hello, | | I am looking for the surface resistivity and volume resistivity of standard fr4 as a function of temperature and /or humidity . can any one help? | | | | Frank: Sorry I'm so late getting back to you. | | 1 Use either ASTM D5109-
Electronics Forum | Fri Apr 17 14:12:27 EDT 1998 | Earl Moon
| Is there anybody to help me ? | We have small balls appearing on the boards soldered by | wave soldering machine and it looks that use of nitrogen | is linked to the problem (because without nitrogen, we have no more | problems). | That remind you
Electronics Forum | Mon Apr 15 22:37:27 EDT 2002 | davef
Regarding your customer suditor, it would have been nice if you said something like ... Routinely, our testing shall be less than 1.56 microgram/cm^2 NaCl equivalent ionic or ionizable flux residue, according to TM-650, Method 2.3.35 'Detection And