Electronics Forum | Mon Mar 30 11:39:46 EDT 2009 | rgduval
Is this a sample board that you ran without components? If so, I'd get it back to your board house, and ask them to explain to you what's happening. We never did get to a satisfactory root cause on our issue (at least, satisfactory to me). It seem
Electronics Forum | Fri Jan 06 00:03:10 EST 2023 | SMTA-64419298
Hello Evtimov, sorry...just saw post as I was looking through list...a bit late. I don't know if you ever got your answer. IPC-4552A covers EniG finishes and suggested shelf life. I've referred to these doc's quite a bit. Good spec's ! Yes, I beli
Electronics Forum | Thu Aug 31 09:53:56 EDT 2017 | mgsmtnet1210
Thank you Amalia for your reply but we are not looking any metals for pcb, we are looking specially Tin plating solution for plating purpose. If you do carry this please give your contact info. Regards, Hetal
Electronics Forum | Tue Dec 13 14:55:12 EST 2005 | muse95
Your response is from the point of view of using a Bismuth solder with Pb plated leads. Samir's point of view is from Bismuth in the plating on the leads being used with a Pb solder. There is a very large difference in the amount of Bi that will en
Electronics Forum | Mon Feb 27 06:42:37 EST 2006 | Slaine
What are the long term issues with high tin content solders on parts plated with silver over copper? Is it possible that the silver will be absorbed by the solder then over a long period of time the tin will react with the copper causing it to part
Electronics Forum | Thu Aug 03 07:47:38 EDT 2017 | mgsmtnet1210
Hello Everyone, Does any one know supplier of Immersion Tin plating solution in North America? Thank you in advance.
Electronics Forum | Thu Aug 03 12:51:07 EDT 2017 | mgsmtnet1210
Thank you so much.
Electronics Forum | Tue Feb 01 12:00:01 EST 2000 | K. Ckak
Hi Folks, I am looking for some info. and possibly a source on measuring inprocess copper plating thickness for Flex PCB manufacturing facilities. I have tried XRF, E-Current method but the supplier told us that it wont work with Flex material - th
Electronics Forum | Mon Dec 12 14:04:33 EST 2005 | craigj
Hi All was wondering is there anything I should be aware of or look out for if using parts with SnBi (Pb free) lead plating with Sn/Pb/Ag solder paste? I was always lead to believe that mixng lead and bismuth caused problems or are the bismuth levels
Electronics Forum | Mon Feb 27 09:31:10 EST 2006 | Slaine
on sections ive looked at with 7 microns of silver and 4microns of copper, the silver had been totally absorbed into the solder in most places and a large amount in some places all the copper as well, so i think the answer is that to provide long ter