Electronics Forum | Tue Aug 17 12:27:48 EDT 2010 | namruht
That reminds me...We already have home plate apertures on our stencil. Try number 2...I tried an overall reduction based on the copper layer of 10% and used oval apertures. I hope that you guys can suggest something that I am over looking. I know tha
Electronics Forum | Tue Aug 17 13:36:17 EDT 2010 | hegemon
Since you have home plated the apts and done solder reduction, I would take a look at your soldering profile. We have run into this before when running no-clean and found that reducing the initial ramp rate to the flux activation was a help in the
Electronics Forum | Sat Aug 21 15:02:32 EDT 2010 | jry74
I have a pcb with 750 plated through holes that get Holtite sockets inserted into them. I have a method of pressing in 10 sockets at a time. However, when we are done, the board has bad warpage on the X and Y axis. Does anyone out there have any t
Electronics Forum | Fri Oct 15 11:03:50 EDT 2010 | hegemon
Well, we got the baking part right at least. I would think that would help to rule out the barrel cracks allowing moisture escape. Plating too thin makes sense to me. In any case, do you think barrel cracking would be observable on a bare PCB?
Electronics Forum | Mon Nov 29 10:13:02 EST 2010 | vetteboy86
My research starts here. I'm just beginning to research the effects of using a leaded part in a no lead process. Before I began, I know there are temperature differences. The part in question has a 260 C spec. Next I would like to find out if any c
Electronics Forum | Tue Jan 25 20:10:30 EST 2011 | markyen
I have an old philip Topaz, not X or Xi. Does anyone have an easy to follow Calibration procedure? I have a manual, glass plate and program but trying to understand the manual is a completed waste of time. This manual must be translate from Japanese.
Electronics Forum | Thu Apr 07 02:38:20 EDT 2011 | aungthura
I didn't know the difference for BGA. We found solderability probelm as show in attach.Then, we called to PCB maker and they said that it could be caused because of PCB finishing. Do you agree this probelm was happend because of PCB finishing? Unfor
Electronics Forum | Thu Apr 07 09:04:19 EDT 2011 | mosborne1
First of all you need a new board house. You should quote us http://www.americancircuits.com. This really looks like a poor drilling operation with the blow holes. Blow holes are usually caused by two main problems. Improper drilling and/or moisture.
Electronics Forum | Fri Aug 19 02:16:40 EDT 2011 | ppcbs
In my opinion destructive methods went out with the stone age. At least they did at our company. We specialize in non-destructive defect analysis. We can determine where the failure is i.e. assembly process, fab defect, BGA defect or plating proce
Electronics Forum | Mon Aug 22 13:28:47 EDT 2011 | scottp
No, don't put weight on it. If the part is really "floating" on the solder and not wetting properly and the solderability looks good on all your other parts then I'd suspect a part problem. Get with the QFP supplier and make sure the Sn isn't too t