Electronics Forum | Mon Jun 30 08:55:31 EDT 2008 | davef
It will be tough to find a dimensional thickness specification for HASL. IPC-6012 Table 3-2, line "Fused tin-lead or solder coat - Coverage and Solderable" states the requirement that there has to be complete coverage of solder on the land, and it mu
Electronics Forum | Fri Mar 03 09:48:06 EST 2000 | Wolfgang Busko
I have heard about it. The main reason is to save money. The problem is, or better is said, that the mixing isn�t that simple for you got have a homogen paste afterwards and the solderballs shouldn�t be deformed in size so that problems during printi
Electronics Forum | Fri Mar 03 09:48:06 EST 2000 | Wolfgang Busko
I have heard about it. The main reason is to save money. The problem is, or better is said, that the mixing isn�t that simple for you got have a homogen paste afterwards and the solderballs shouldn�t be deformed in size so that problems during printi
Electronics Forum | Thu Jan 12 10:05:13 EST 2006 | davef
There's a lots comparisons like this on the web. Here's one: Westwood Associates said on 8/12/2003: ||HASL||OSP||ENIG||Pd||Tin||Silver Flat||no||yes||yes||yes||yes||yes Solderjoint||Cu-Sn||Cu-Sn||Ni-Sn||Ni-Sn||Cu-Sn||Cu-Sn Contact||E-test, ICT||no|
Electronics Forum | Fri Feb 18 13:55:12 EST 2022 | cbart
One thing to think about is keeping the machine running! the biggest thing I would be looking at or into is availability of spare parts and tech support. Call the equipment manufactures and see if they are still supporting the machines, both with tec