Electronics Forum | Fri Mar 07 14:48:34 EST 2003 | gdstanton
Pretty much everything under the sun. For example if Company A wanted to hire Company B to build printed circuit cards designed by Company A; What type of T & C might Company B seek in their contract/agreement with Company A? The following things c
Electronics Forum | Fri Jul 28 14:34:13 EDT 2000 | Gary Simbulan
Belive it or not, these boards were run through a Centech batch mode Vapor Phase machine. Single stage top side IR preheat. Vapor temp 218 C. Solder paste is an SN62 RMA.The boards were FR4 8 layer w/ solder mask, fairly conventional as might be e
Electronics Forum | Tue Apr 13 18:39:24 EDT 1999 | Tom B
| | Netters, | | | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | | | 1. Kester 293 no clean | | 2. 2.1 C/s for 30s to 150 C | | 3. .5 - .7 C/s f
Electronics Forum | Tue Apr 13 23:08:56 EDT 1999 | Jeff Sanchez
| | | Netters, | | | | | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | | | | | 1. Kester 293 no clean | | | 2. 2.1 C/s for 30s to 150 C | | | 3.
Electronics Forum | Thu Aug 01 13:04:57 EDT 2002 | gdstanton
Its interesting. It appears I'm getting conflicting feeback from Indium. This says its not a problem... http://indium.custhelp.com/cgi-bin/indium.cfg/php/enduser/std_adp.php?p_sid=kTDKGClg&p_lva=&p_faqid=355&p_created=1014734692&p_sp=cF9ncmlkc29
Electronics Forum | Mon Jul 13 06:30:59 EDT 2009 | hcarrasco
1.- Check your vacuum a.- Check filters b.- Check air flow (the vacuum is generated by a Ventury using air flow, not air pressure) c.- Vaccum vias (Possible linth inside the vacuum lines) 2.- Check the nozzle condition (Probably broken o
Electronics Forum | Mon Nov 27 17:47:23 EST 2000 | Dave F
Gyver: Lemme take a wack [if you�ll excuse the expression, given direction of the later discussion] at your questions. Q1. Will the baking of BGA or PCB cause more oxidation before the SMT process? A1. It certainly will not cause less oxidation,
Electronics Forum | Sat Aug 29 08:43:35 EDT 1998 | Dave F
| Hi, Friends, | Could you please recommend me some solder mask materials and equitements for high quality solder mask? Details such as company name, phone numer et al are welcomed. Thanks! | Have a good day | Xingsheng Xingsheng: Consider the follo
Electronics Forum | Sat Jul 17 15:22:17 EDT 2004 | rohman23
Thanks for all the responses. I do agree with what was said, and can certainly see reasons not to try. I'll write a little more about what we do. We are a defense contractor, and as I mentioned very high mix, low volume. We only have 1 SMT line.
Electronics Forum | Fri Jul 02 08:24:16 EDT 2004 | davef
HyperBGA: http://www-306.ibm.com/chips/techlib/techlib.nsf/techdocs/852569B20050FF7785256996004C8AFA/$file/hyperbga.pdf SuperBGA: http://www.amkor.com/Products/all_products/sbga.cfm
.gif)