Electronics Forum | Fri Aug 01 21:10:35 EDT 2008 | leo_dektec
You can keep only the 5th zone as the reflow zone. And lower the first two zones to keep a good ramping rate. Meanwhile,please note the ting temperature in software or control panel is not the exact temperature in your PCB, you'd better get a KIC or
Electronics Forum | Fri Jul 25 23:01:04 EDT 2008 | chip_flip
What paste are using? You should referance the manufactures time and temperature specification. Running lead-free in a 5 zone oven can be done with out a problem but it is not production friendly. If you are concerned with through put I would look fo
Electronics Forum | Sat Aug 02 08:06:11 EDT 2008 | pcbbuilders
Is there a limit to the time that most components can stay at temperatures around 130-200 deg c? if i slow the time, the first 4 zones will be at this temp for about 5 minutes in no lead process. i am concerned that some chips wont be rated at this t
Electronics Forum | Mon Aug 04 09:30:16 EDT 2008 | grics
If you have concerns, you can look at the datasheet for each component or contact one of their application or materials engineers and find out what the components are rated for...process-wise. IE, how long can I be in the oven with this part, at what
Electronics Forum | Tue Aug 22 14:59:55 EDT 2000 | Mike Naddra
What does the reflow profile look like , the question I had was surrounding the higher reflow temperature and the max temperature that lowest thermal mass components will see. Some other questions that I had were surrounding the components , what of
Electronics Forum | Thu Apr 18 23:56:27 EDT 2002 | Abelardo Rodriguez
I'm trying to get a better understanding of the cooking process of pcb's. The use of nitrogen in reflow and wave ovens. Seems to have a wide margin of acceptance as a standard gas to prevent oxidation of metals in the board. Has any one heard or us
Electronics Forum | Fri Oct 30 15:09:44 EST 1998 | ChungPark
| Dear all, | | What are your views on reworking BGA's? I mean, with the BGA going through reflow temperatures four times or more, and with a manual reballing process, wouldn't it raise up a few reliability issues? Would you consider not doing rew
Electronics Forum | Tue Aug 22 16:02:07 EDT 2000 | Dr. Ning-Cheng Lee
If the thermal mass of the products is small, a tent-shaped profile is recommended, with peak temperature around 240C. The hottest spot on board should be less than 250C. However, if the thermal mass of the product is large, such as a large server PC
Electronics Forum | Tue Jan 31 12:37:33 EST 2006 | carterhoward
I guess my biggest concern would be what will happen to the inner metallic layer of the leaded solder during the higher temperatures.
Electronics Forum | Thu May 13 20:40:25 EDT 2021 | winston_one
Yes, we can't use pure Pb PROCESS. And as I say we will not use it anyway, as we have lead-free BGA's, LGAs, component with Solder Charged Terminations... It's became almost normal practice to solder it with leaded solder pastes. In this case peak re