Electronics Forum | Mon Feb 18 15:44:49 EST 2008 | ck_the_flip
Yup! All the major players out there - KIC, Datapaq, and ECD - are all capable of profiling both reflow and wave solder. check them out. www.kicthermal.com www.ecd.com www.datapaq.com
Electronics Forum | Wed Sep 25 10:56:27 EDT 2002 | xrayhipp
Yeah, perhaps lean more towards a ramp-to-spike profile - reducing the soak time and add a littel heat to your temp above liquid. This has worked for us with water soluable paste as we are not required to use no-clean and utilizing a 6-zone oven. G
Electronics Forum | Wed Sep 25 06:56:16 EDT 2002 | CH
U may check your profile ramp rate. The flux may evporated and look like cold joint
Electronics Forum | Fri Feb 17 09:02:21 EST 2006 | russ
proper pad geometries, accurate placement, and good reflow profile. Are you having problems right now?
Electronics Forum | Fri Dec 15 18:36:46 EST 2006 | Grant
Hi, I have noticed we are getting residue on our wave pcb's and it's worse with lead free, since we changed to the flux we are using. We are currently using Avantec VOC Free flux model Ecofree 303. It looks like it's made in Malaysia. Does anyone h
Electronics Forum | Sun Dec 17 18:16:27 EST 2006 | greg york
can you describe the residue more for me cheers greg blt circuit services
Electronics Forum | Wed Dec 20 12:25:16 EST 2006 | Polynesian Pebbles
Hey pr, what cha slicin' these days besides your tee shots (and your bread)? LOL
Electronics Forum | Wed Dec 20 12:52:18 EST 2006 | pr
Been known to dice a flip or 2. (and we're playing in 70 degree weather)!
Electronics Forum | Tue Feb 19 09:41:26 EST 2008 | slthomas
ECD sells the MOLE, and they sell both the Oven Rider and the Wave Rider to accompany it. The thing is, you can profile both an oven and a wave machine without either if you're willing to just solder your thermocouples to a board. The nice thing ab
Electronics Forum | Wed Dec 20 04:43:36 EST 2006 | greg york
Any decent flux would volatise off with the heat of the wave unless absorbed into the solder mask. Test this by trying to clean in alcohol or common solvent aerosol, if it does not clean then it is probably Mineral Salts from solder mask fillers. Ano
.gif)