Electronics Forum | Fri Apr 01 18:32:51 EDT 2011 | frcdave
Dback, Some questions for you: 1. Are you using the red light configuration for better contrast on the 0402 parts? 2. Is your system fitted with both low and High Magnification cameras? Have you spoken with the guys at YESTech? Their phone support i
Electronics Forum | Fri Oct 31 07:52:23 EDT 2008 | davef
For a better understanding of decoupling capacitors, look here: * http://en.wikipedia.org/wiki/Decoupling_capacitor * http://www.hottconsultants.com/techtips/decoupling.html * http://pcdandf.com/cms/content/view/3410/95/
Electronics Forum | Mon Apr 04 11:46:20 EDT 2011 | frcdave
I was thinking the same thing. Try turning off your anchors and look at the size of your search and % match you have set. if you are concerned about not catching missing components, try training a negative template.
Electronics Forum | Mon May 09 09:23:45 EDT 2016 | markhoch
I agree with the previous two replies. This is a perfect design....if you're trying to create a graveyard full of tombstones.
Electronics Forum | Thu Oct 30 15:36:18 EDT 2008 | grantp
Hi, Sounds like your engineer does not know what he's doing. We have developed and built hundreds of thousands of boards with normal square pads for 0402, and we just use a 5 thou stencil with 5% reduction and it works well. Decoupling? What is tha
Electronics Forum | Fri Mar 06 10:50:21 EST 2009 | fountain42
Just my opinion but it look's like your doing a great job. i would try another paste. I'm somewhat lucky that we get to use OA's. If your stuck using the no-cleans they are so tempermental. (The nitrogen is making up for the poor paste) Your de-wetti
Electronics Forum | Thu Jul 20 14:57:26 EDT 2000 | Bob Willis
I have just measured my new test board and the dimensions are 0.025� square, 0.015� seperation with resist aperture 0.004� larger. Don�t know when I will be using it yet. I have not seen a head to head with these pastes yet, I know that Panasonic ar
Electronics Forum | Thu Mar 05 11:53:09 EST 2009 | dcell_1t
Hello to all. for certain time, we have been struggling with some issues on a PCB where have tombstoning on 0402 components (due to pad design) and dewetting in qfp256 0.5 mil pitch (discussed on another threads on this forum) component, we have pro
Electronics Forum | Fri Mar 06 02:47:15 EST 2009 | lococost
Have you tried higher peaktemp? I saw the QFP is sn90pb10, This has a liquidus of 268 - 302 C. A good paste should be able to handle 230C (or more), of course you would need to check your other components peak temp.
Electronics Forum | Fri Mar 06 11:01:53 EST 2009 | dyoungquist
I have attached a pdf version of an article that explains the basics of a nitrogen atmosphere when soldering. It gives some basic guidlines as to when one may want to use nitrogen and what it can and can not accomplish. FYI- I did not write that ar