Electronics Forum | Sun Jan 31 22:55:33 EST 1999 | Dennis O'Donnell
| | Hello Netters, | | | | I need some info, Earl or Dave, I have a PCB that exhibits a white layer on solder side. It does not appear to be surface residues (IPA has no effect), but looks like its under solder mask. My first guess is that the LPI
Electronics Forum | Wed Feb 03 04:44:43 EST 1999 | Jeff Sanchez
| | | Hello Netters, | | | | | | I need some info, Earl or Dave, I have a PCB that exhibits a white layer on solder side. It does not appear to be surface residues (IPA has no effect), but looks like its under solder mask. My first guess is that t
Electronics Forum | Fri Sep 11 15:11:23 EDT 1998 | Dave Celestian
I am running composite fixtures on my wave solder machine and after about 500 passes each (1 month)they are showing serious signs of wear in that the composite surface is bubbling up and glass fibers are also starting to show. The problem here is t
Electronics Forum | Mon Sep 14 09:09:10 EDT 1998 | Earl Moon
| I am running composite fixtures on my wave solder machine and after about 500 passes each (1 month)they are showing serious signs of wear in that the composite surface is bubbling up and glass fibers are also starting to show. | The problem here
Electronics Forum | Fri Sep 11 15:26:15 EDT 1998 | Upinder Singh
Dave, What exactly is the material used for making the fixtures? Upinder ====================== | I am running composite fixtures on my wave solder machine and after about 500 passes each (1 month)they are showing serious signs of wear in that the co
Electronics Forum | Fri Jul 23 05:14:40 EDT 2004 | greg york
Hi Thomas Ever considered that this maybe HASL flux left on PCB as this is extremely hygroscopic and has heat transfer fluids that cannot be baked out unless you go to a temperature of around 600C. One way of testing is to leave iron tip on joint an
Electronics Forum | Tue Nov 11 19:41:06 EST 2008 | gregoryyork
Thats the problem residual residue from HASL fluxes Lead free especially are worse.Very hygroscopic and out gass and produce dewetting as well over wave soldered boards especially. Leave iron on blown joint and will after several seconds fizz and pop
Electronics Forum | Thu Oct 02 21:00:26 EDT 2003 | davef
Who says the chlorine comes from your tap water? Our PTOW dumps boat loads of chlorine into our water periodically. Sometimes it's so bad you can smell it. We doubt that it is the source of your problem. This chlorine will volitize very quickly,
Electronics Forum | Fri May 14 14:52:56 EDT 1999 | Ryan Jennens
| | | | I am looking for anyone who has converted over to VOC Free flux. I need some info on any problems, etc. that you might have had. | | | | | | | | Please E-mail me at wes.ruggles@vickers-systems.com or call at (513) 494-5229 | | | | | | | | T
Electronics Forum | Tue Sep 15 08:59:59 EDT 1998 | Chrys
| I am running composite fixtures on my wave solder machine and after about 500 passes each (1 month)they are showing serious signs of wear in that the composite surface is bubbling up and glass fibers are also starting to show. | The problem here