Dross Eliminator

Electronics Forum | Thu Sep 07 16:50:44 EDT 2006 | greg york

Just reading these comments are really interesting but very baffling. That if the solder manufacturers produces solder which 'is' actually Virgin high quality material and treated with conventional metallic anti drossing agents AND continue to add th

Chinese Wave Solder Machines

Electronics Forum | Mon Nov 27 16:52:18 EST 2006 | greg york

Hi Bill Mostly in the UK, but originally saw the problem when I helped on one install in Malta on a chinese mc set at 5 degrees and had nightmare bridging. changed the angle to 6.5 ish and results were instantly better actually better than what they

Wave Solder - solder bubbles/outgassing??

Electronics Forum | Tue Nov 21 19:23:15 EST 2006 | greg york

Had exactly the same problem the other week. Baked some boards did improve slightly but not convincingly. Washed bare PCb and found excessive HASL fluids left on board from improper rinsing and problem disapeared. Baking HASL fluid out is impossible

AuSn Alloy Solder Electroplating

Electronics Forum | Wed Sep 29 17:59:59 EDT 2004 | gregoryyork

I would be interested in this as well. Can you forward me some details. thanks Greg York Technical Sales Manager BLT Circuit Services Ltd - UK

Solder Analysis

Electronics Forum | Wed Jan 18 17:35:08 EST 2006 | gregoryyork

We manufacture solder and dont charge, so agree with the others and change elsewhere just make sure you are changing to better material if unsure stick with what you have and pay for it under duress. Cheers Greg York BLT Circuit Services Ltd England

OT: Wavesolder Process Engineer Needed

Electronics Forum | Thu Jul 10 10:39:47 EDT 2008 | gregoryyork

Whats the money like, I would do anything to get away from the Bureaucrats from Brussels running our country. Best regards Greg York

lead free 0603 wave soldering

Electronics Forum | Tue Dec 09 19:04:54 EST 2008 | gregoryyork

you need to check your angle on this, can you measure and advise what you have cheers Greg York


Electronics Forum | Thu Dec 10 06:01:22 EST 2009 | gregoryyork

have you checked solder resist cure as this will cause the glue to lose adhesion if not cured correctly especially if dwell time sin the wave are excessive i.e 4-5 seconds cheers Greg York


Electronics Forum | Tue Jul 29 05:04:20 EDT 2003 | gregoryyork

Dear adam Sounds to me like it may not be Salt water contamination or even flux residue's, as both of these are commonly cleaned semi aqueosly or with IPA. Have you considered it may be Talcum powder used as fillers in solder resist, mineral salts

Solder wave

Electronics Forum | Mon May 07 11:08:13 EDT 2007 | gregoryyork

Are the pallets hot and killing the foam head as they pass over or is the air pressure on the air knife toi high travelling back along the board killing the foam. If these are OK make sure you have sufficient back flow onthe wave and you are draining

greg york searches for Companies, Equipment, Machines, Suppliers & Information

High Throughput Reflow Oven

High Throughput Reflow Oven
Software for SMT

Nozzles, Feeders, Spare Parts - Siemens, Fuji, Juki, Yamaha, etc...
Global manufacturing solutions provider

World Source Equipment: Used equipment sale. Hundreds of items on sale.
Dual Lane Reflow Oven

Reflow Soldering 101 Training Course