OSAKA, JAPAN � March 2008 � Nihon Superior USA, a subsidiary of Nihon Superior Co. Ltd., an advanced soldering supplier to the worldwide market, announces that it will showcase a new, expanded range of SN100C products in booth 249 at the upcoming APEX exhibition and conference, scheduled to take place April 1-3, 2008 in Las Vegas.
Electronics Forum | Thu Nov 29 17:30:07 EST 2001 | davef
You give no clue of what you want to write about. Let's try this: J-STD-001, 8.3.1 Particulate Matter says words to the effect of solder balls / splats shall be neither: * Loose or able to be dislodged during normal service � NOR * Violate minimu
Electronics Forum | Tue Nov 04 12:58:17 EST 2008 | smt123
I have to agree with Patrick here. This image appears to show a board that is NOT HASL as there is what appears to be a copper pad in the upper portion of the image. But then again the arrow tip appears to be white and I woudl expect that to be red s
Electronics Forum | Thu Oct 30 19:59:05 EDT 2008 | gregoryyork
solder ball was caused by hasl process not reflow. seen before many times, look around wells of smt on bare boards should be more of them
Electronics Forum | Thu Oct 23 23:38:48 EDT 2008 | pathakvj
We have 8 layer HASL PCB. We saw molten solder blobs / balls on op side of assembled PCB. (to check, if this was a bare board problem), We passed bare board as received thru, SMT reflow oven and saw solder balls on top side of board. What could be th
Electronics Forum | Fri Oct 24 06:55:48 EDT 2008 | clampron
Good Morning WS, If you experieced the solder balls after reflow of a bare board through the oven, then the source of the solder is either the oven or the board. I have had boards with untented via's that were HASL'd that had entrapped solder and fl
Electronics Forum | Tue Jul 15 15:46:05 EDT 2008 | slthomas
Can you describe your solder balls...mid-chip solder balls, "splatter" around pads, etc.?
Electronics Forum | Wed Nov 20 09:23:53 EST 2019 | alpha1
We had a board we fought with for a while with solder balls. Checked everything, Stencil thickness at .004, reduced apertures, changed paste 3 times, changed profile 3 times. Finally changed board vendors. Went from HASL to Emersion Gold. Problem sol
Electronics Forum | Thu Jun 22 15:05:55 EDT 2017 | solderingpro
There are several different technologies in the industry today to assist in the out-gassing of flux cores. On automated soldering systems, there are two main types of perforating solder feeders: - Hole Drilling - "V" Scoring By perforating the so
Electronics Forum | Thu Sep 16 15:01:13 EDT 2004 | russ
You may want to either open up the bottom of the vias so they will not "volcano". Or you will want to seal both sides. It never works having one side of the vias masked and the other open with HASL. Russ