Electronics Forum | Fri Aug 14 08:59:51 EDT 1998 | Dave F
| | | Hi, can you please tell me how to make green coating and through-hole plating of PCB? Thanks! | | | Xingsheng | | Xingsheng: Welcome. | | Bible on PCB fabrication: Printed Circuits Handbook, Clyde Coombs, McGraw-Hill | | Web resources: htt
Electronics Forum | Fri Jan 15 15:06:30 EST 1999 | Earl Moon
| Hello, | | We are qualifying new sources of PWB vendors. We've got the first lot of "produciton" boards in and we want to put them through the paces before turing the vendors on. | | So far, the tests I can think of performing, and that we have
Electronics Forum | Fri Jan 15 15:17:21 EST 1999 | Earl Moon
| | Hello, | | | | We are qualifying new sources of PWB vendors. We've got the first lot of "produciton" boards in and we want to put them through the paces before turing the vendors on. | | | | So far, the tests I can think of performing, and tha
Electronics Forum | Thu Feb 11 09:45:06 EST 1999 | Dave F
| | | Helo, | | Is it common for actual print height of solder paste to exceed the stencil thickness. For example If the stencil is 6mill thick and the actual height of the print is apx. 10 or 11mill. What causes the paste height to be greater t
Electronics Forum | Thu Sep 09 10:09:15 EDT 1999 | John Thorup
| | | I have a board that has surface mount on both sides . On this board is a 22pin connector which is the only thru-hole part.This part is located on the component side. I would like to reflow this part. Can this be done? If so, how can this be don
Electronics Forum | Fri Oct 11 09:28:14 EDT 2002 | davef
Designers love to do BIG copper pours for several reasons: * Maximize heat spreading. * Increase EMI shielding. * Laziness. The poor folk that solder the parts on boards HATE big copper planes near solder pads. During soldering, fat copper traces [
Electronics Forum | Thu Mar 23 22:26:53 EST 2006 | Joseph
Dear all, Referring comment from Mr. Jack,IPC director certification & assembly technology, the term "fillet tearing" is too broad. Cracks or fractures in the required fillet area, with SnPb or LF alloy and whether you call it tearing or not, is a D
Electronics Forum | Tue Apr 27 16:44:05 EDT 1999 | Chrys Shea
| | Has anybody had experience wavesoldering 1 watt 2512 resistor packages?? I know it can be done, but are there reliability issues? | | | | We are in the middle of a new product and the question was posed to me "Can we use 2512 1 watt resistors o
Electronics Forum | Thu Jul 05 19:39:19 EDT 2001 | davef
I had forgotten that it was you that was on the Sipad adventure. [But then again, who can keep track of yer aliases? ;-)] You just go from one adventure to the next. Expanding On Dave�s Hi-Test Flux Method Theory � PASTE: Yes, contact your favorit
Electronics Forum | Fri Jan 15 16:55:50 EST 1999 | Chrys
| | | Hello, | | | | | | We are qualifying new sources of PWB vendors. We've got the first lot of "produciton" boards in and we want to put them through the paces before turing the vendors on. | | | | | | So far, the tests I can think of performin