Electronics Forum | Sat May 28 06:43:03 EDT 2005 | steve
I have the ability to offer both SAC and SN100C lead free alloys to my customer base. What might occur if a customer is already using SAC305 in their wave and they want to save money and go to SN100C. They now are mixing, tin,silver,copper with tin,c
Electronics Forum | Fri Feb 22 15:16:24 EST 2002 | rkevin
Bet your using tin/ lead plated components with a lead free Cu/Ag/Sn alloy. It leads to intermetallic cracking. Wow didn't anyone tell you to check the archives yet, It seems to be the answer given to everyone. Why have an interactive site if you alw
Electronics Forum | Wed May 24 16:47:21 EDT 2006 | patrickbruneel
Inds, It's about time that lead-free components can stand higher temps "myth" stops. The only difference is the plating, the component itself has not changed. Can you give us an update on this threat? If you�re the same inds http://www.smtnet.com//
Electronics Forum | Wed May 24 16:19:58 EDT 2006 | inds
John, there have been quite a few discussion on Mixed Assemblies in this forum.. do a search.. you will get whole lot of information.. in addition - IF you are using Lead-free reflow profile...make sure the rated temp for Sn-Pb components is not vi
Electronics Forum | Fri Feb 17 11:01:47 EST 2006 | amol_kane
with lead-free solders, one would expect to find less instances of tombstoning. this is because SAC alloys are not eutectic and melt over a range of temp (usually 217-220 deg C) instead of at a single temperature. therefore the forces due to solder s
Electronics Forum | Fri Dec 05 11:27:10 EST 2008 | patrickbruneel
Every problem faced with (all) lead free alloys can be solved with 2 words �add lead� I'll keep it short don't want to sound like a broken record.
Electronics Forum | Tue Jul 12 08:44:58 EDT 2005 | jdengler
JBC is offering "Lead free" tips now. They have this on the web site: "JBC recently released a new series of tips featuring a thicker iron bath that we find more resistent to aggressive additives and flux as found in lead free alloy." We have not d
Electronics Forum | Tue Jul 12 06:13:30 EDT 2005 | dougs
A while back we checked out all our manufacturing equipment for lead free capability, we thought our soldering irons would all be fine as they can reach temperatures well in excess of lead free alloy melting points. Last week i was speaking to someo
Electronics Forum | Tue Aug 31 17:36:36 EDT 2004 | davef
NO-LEAD COMPONENTS WITH LEAD SOLDER ISSUE: We agree with Russ. We've dicussed this several times on SMTnet. For instance, look here http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=25394 LEAD COMPONENTS WITH NO-LEAD SOLDER ISSUE: We disa
Electronics Forum | Mon Dec 22 10:43:18 EST 2008 | etechsupply
I wanted to hear from users of the SN100C alloy to find out what they think is positive and negative about this lead free alloy. Thanks, Keith