Hi wolfgang,Dave & PC: What I facing are: 1. The component lie flat on the board but only one side can get solder.The pad is ok, problem is with the chip. 2.I desolder the chip and go to view it under microscope and found that there is a line near t
Electronics Forum | Fri Oct 01 17:59:13 EDT 2010 | rway
Your real problem is further upstream. The limitations of your AOI aside, first find out why your leads are being lifted. Is it through handling or are they from the reel that way? To address your AOI question, Hegemon is correct, coplanarity inspe
Electronics Forum | Sat Apr 04 08:35:27 EDT 2009 | davef
Cause: Solder between the pad and the BGA on the pads being lifted has not melted. So, when you lift the BGA, you also lift those pads with the unmelted solder with the BGA. These pads are probably sinking the heat to a large copper plane in a inner
Electronics Forum | Mon Apr 06 11:46:10 EDT 2009 | c111
I agree the longer soak will help provided you are not applying to much heat/time to the board now. -are the pads that lift connected to anything? This has happened to me in the past where un-connected pads would come of far easier than those connec
Electronics Forum | Fri Apr 03 15:30:10 EDT 2009 | ed_faranda
I have a VJE Summit 750 Rework machine... I don't think that matters much, but I put it out there anyway. I am removing a BGA (29mm x 29mm) off a board, but some of the pads on the board are being lifted during the process. Does someone have any
Electronics Forum | Thu Apr 09 07:37:18 EDT 2009 | fowlerchang
Another suggestion for it. Baking the whole boards before rework the BGA. It is not only benifit to the BGA but also to the pad.
Electronics Forum | Thu Apr 09 09:23:29 EDT 2009 | ed_faranda
Well, I did manage to solve this problem. I lowered the max boards temp from 245 to 235. Then I decreased my TAL. This seemed to work perfectly. Thanks everyone for your suggestions! They got me in the right direction.
Electronics Forum | Wed Apr 08 15:16:14 EDT 2009 | waveroom
I would use almost the same profile you use when putting the component down on the board. Your pre-heat is essential in rework. Also even though your machine tells you your at a specific temperature I would add a thermocouple next to the component yo
Electronics Forum | Mon Apr 06 11:53:50 EDT 2009 | ed_faranda
Here are some pictures of the part. I created a profile for this part. I've been in touch with the vendor and he seems to think the profile is too hot. I am waiting for another board from R&D so I can work on it again. If you look at the picture,
Electronics Forum | Sun May 30 08:50:42 EDT 1999 | Dave F
| Yes l know this problem keeps cropping up on the forum but l've missed some of the follow-ups. | | Our problem is that the lifting only occurs on 3% of production so actually detecting an improvement is difficult. We're actually having to inspect