Electronics Forum | Mon Jun 08 14:19:30 EDT 1998 | Gary Simbulan
Earl, et al, Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. First the caps. We still have
Electronics Forum | Mon Jul 19 12:37:15 EDT 1999 | Wolfgang Busko
| | | | | Hi, SMTASSY | | | | that�s what we do, soldering our double-sided-finepitch-BGA-and all-the-other-stuff-boards in vapourphase because it�s the only thing we have. | | First, we do not do real series produktion, only prototyping up to som
Electronics Forum | Tue Jul 20 05:29:14 EDT 1999 | Wolfgang Busko
| | | | | | | | Hi, SMTASSY | | | | | | that�s what we do, soldering our double-sided-finepitch-BGA-and all-the-other-stuff-boards in vapourphase because it�s the only thing we have. | | | First, we do not do real series produktion, only prototypi
Electronics Forum | Wed Aug 27 13:11:19 EDT 2008 | dwelch123
We roll ours up, fingers and all, and soak them for about an hour in a solution of water and DOMINATE (heavy duty degreaser) you can order from Grainger. They come out looking brand new every time!
Electronics Forum | Sun Jul 12 21:15:31 EDT 2009 | padawanlinuxero
a more general solution is have you done some cleanning in the vaccumm for the nozzles? change the filters or filter?
Electronics Forum | Tue Dec 03 10:22:25 EST 2013 | cpitarys
Insure your rinses are only 25 to 30-seconds each. Also there are options for cleaning solutions from Kyzen that are safer on AL and do not require dosing of any additional inhibitors.
Electronics Forum | Tue Aug 30 10:46:27 EDT 2005 | lyrtech
Hi, I curently have an interesting challenge. But I don't have all the knowledge to solve it. One of our boards is used in RF applications. We noticed that the No-Clean flux residue makes interferences in the RF signal. Removing the flux residue so
Electronics Forum | Fri Mar 06 10:50:21 EST 2009 | fountain42
Just my opinion but it look's like your doing a great job. i would try another paste. I'm somewhat lucky that we get to use OA's. If your stuck using the no-cleans they are so tempermental. (The nitrogen is making up for the poor paste) Your de-wetti
Electronics Forum | Tue Jan 08 09:23:18 EST 2013 | lock_2002
This is a question regarding soldermask between pins of fine pitch devices. The majority of our production designs end up with at least 2-3 mils of copper thickness on the external layers due to blind vias, wrap plating requirements, etc. Our curre
Electronics Forum | Tue Jun 16 15:01:58 EDT 1998 | Gary Simbulan
There are some common reason for capacitor cracking on my web page if you want to have a look. The document can be downloaded for your reference. | Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior