Electronics Forum | Mon Aug 09 10:10:29 EDT 1999 | Gian.D
hello to everybody, we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; does anybody know how to eliminate flux residues or how not to produce them during rework operations? Th
Electronics Forum | Tue Aug 10 07:47:12 EDT 1999 | Brian
| | | hello to everybody, | | | we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; | | | does anybody know how to eliminate flux residues or how not to produce them during rew
Electronics Forum | Tue Aug 10 20:22:15 EDT 1999 | Wayne Sanita
Hello, Could be that touchup operators are using too much flux. What are you dispensing flux with. Disposable or refillable flux pens are good to have around. | | | | hello to everybody, | | | | we have a really satisfactory no clean proc
Electronics Forum | Thu Aug 12 09:02:08 EDT 1999 | Gian.D
| Hello, | | Could be that touchup operators are using too much flux. What are you dispensing flux with. Disposable or refillable flux pens are good to have around. | |Good! could you suggest some suppliers name or address or web site or e.mail...
Electronics Forum | Mon Oct 22 11:47:59 EDT 2007 | brulal1
Thank you guys for your help, I do not clean any on my assemblies who are build by the SMT an wave soldering department, we do used liquid fluxes Kester 951 and cored wire keester 245, usually it�s for batteries connector, led, terminal and wire rap
Electronics Forum | Fri Oct 19 13:57:17 EDT 2007 | Michael Konrad
Hi Rob, I must take issue with your statement �By definition, no clean solder can be not-cleaned�. All no-clean fluxes can be cleaned. Whether or not one cleans no-clean depends on a variety of factors. More than eighty percent of all post reflow
Electronics Forum | Wed Aug 18 15:52:21 EDT 1999 | DENNIS FOWLER
| | | Gian | | | | | | You alarm me when you talk of white residues in a "no-clean" process. This should not happen. It sounds like you have compatibility problems between different residues and/or a poorly polymerised solder mask. | | | | | | Ther
Electronics Forum | Fri Jun 19 18:44:23 EDT 1998 | Steve
Does anyone have wave solder experience using OSP and VOC free no clean flux?
Electronics Forum | Wed Aug 10 07:55:21 EDT 2005 | ajaydoshi
we are using heareous F381, F352 no clean solder paste. specially in qfp for high frequency board we observe that cleaing / removing of ' no clean flux 'is require. if we do not clean same most of time after all test & envioumental test it shows pin
Electronics Forum | Wed Aug 10 08:10:39 EDT 2005 | davef
Comments are: * Sounds like it's necessary to clean "heareous F381, F352 no clean solder paste" in your application. Consider a paste that may be better suited to your application. * If you're cleaning "low residue flux", consider using an organic ac