Electronics Forum | Mon Apr 09 20:55:46 EDT 2012 | action_101
I forgot to add that we are using a 3 mil stencil. It seems like to me that may be there isn't enough flux left when we reach liquidous?? About half of the solder spheres do melt and wet on each pad, but the top half of each solder joint is just the
Electronics Forum | Mon Apr 09 21:09:29 EDT 2012 | isd_jwendell
I haven't worked with anything as small as 01005s, but something you didn't mention is the %metal of your paste. I just switch from 90% to 89.5% (AIM NC257-2) and could tell the difference. Just an idea...
Electronics Forum | Mon Apr 09 21:20:59 EDT 2012 | action_101
Interesting thought. Our paste is 89.2% according to the data sheet I have, but it still might be worth trying the 84-86% syringe blend. Thanks for the suggestion.
Electronics Forum | Fri Apr 13 12:31:23 EDT 2012 | markhoch
*Like* (There should be a way to "Like" or "Dislike" replies so that other Engineers can agree or disagree with a response. Doens't this sound like a good idea?)
Electronics Forum | Fri Apr 13 16:52:07 EDT 2012 | hegemon
Hey Frazzled, you mean you don't prefer the back and forth flaming wars when someone disagrees with an opinion? How about "Agree" & "Disagree" for starters. Later we can add "YGTBK"(you got to be kidding), and "WP" (Wrong Planet) Great idea Frazz
Electronics Forum | Mon Apr 16 18:53:14 EDT 2012 | action_101
What is that garbage. How about you add flamer to like and dislike. I would have used it at least 3 times in this thread alone.
Electronics Forum | Wed May 03 20:24:22 EDT 2000 | Dave F
MF: I know of nothing that addresses your question directly. Let me suggest: * Technical types at your solder supplier should be able to help. * "Effect Of Intermetallic Compounds On The Thermal Fatigue Of Surface Mount Solder Joints" PL Tu, et a
Electronics Forum | Mon Apr 09 19:50:33 EDT 2012 | action_101
Hello, We're building some boards with 01005's and the only issue we are running into is the solder is not reflowing. It's the damnest thing, we are having no issues with the printing process or placing the components, the two areas we thought we wo
Electronics Forum | Mon Oct 16 20:33:18 EDT 2000 | Dave F
MK: If you are getting good product with air, here�s what you should do: * Turn off the N2. * Sell that N2 cracker machine. * Pat yourself on the back. * Go out for beers. [Not any of that Canadian Fosters crap, tho][Did you know that Ozzies do
Electronics Forum | Mon May 24 06:04:09 EDT 2004 | johnwnz
Nitro, I msuggest you get your oven manual out and start reading!! it depends on yoru machine, the point of injection, how many zzones it's designed to cover (some only inject for reflow) what your inward flow rate is, what yoru exhaust rate is and