Hello Did you just buy this machine on the used market? There is a possibility that the stencil is not height on all 4 corners ( from the center nest assembly. I don't under stand " the under stencil wiper is not working correctly". This is about
Electronics Forum | Tue Nov 08 08:48:52 EST 2011 | dwoodbury
No the login dont seem to change anything. It is starting to appear that there is an issue in the communication board itself.
Electronics Forum | Tue Sep 26 08:41:27 EDT 2000 | greg
I am processing PCB's that have an n-tech osp coating and am finding huge inconsistencies in wetting. Some boards process clean with good wetting and the next has terrible wetting. The boards are stored and handled properly. Has anyone had this
Electronics Forum | Fri Aug 10 14:43:27 EDT 2007 | judym
When running some double sided reflow boards through the Heller oven, some of the caps/ res's are falling off the bottom side of the board. I understand if the parts are too heavy they wont stay in the molten solder, but these particular parts are no
Electronics Forum | Tue Jul 17 09:49:21 EDT 2007 | slthomas
We haven't used no-lead yet so I can't speak to the specifics of that part of the equation, but am I the only person here that sees "thick board or a board with a large ground plane" and immediately thinks this is a thermal issue? Am I oversimplifyin
Electronics Forum | Thu Jul 19 17:22:17 EDT 2007 | gregoryyork
You need to dwell the boards longer in the wave as the board is the largest heatsink. Just make sure the flux can take the longer dwell times anything up to 4 - 5 seconds so you may have to shallow your angle as well to around 5 - 6 degrees this will
Electronics Forum | Thu Jan 08 11:06:40 EST 2004 | russ
If I read this correctly you have two identical ovens that were setup the same ie zone temps, fan speeds etc... when you ran the same board through each of them one showed a lower board temp. Is this correct? Is the temp of the board 7 deg. lower t
Electronics Forum | Tue Sep 21 10:53:53 EDT 2004 | davef
We know nothing about Envivar UV 1244 and you weren't real clear about the details of the problem or the materials [eg, ws flux, solder mask, etc], but we'd speculate your adhesion problem goes back to the cleanliness of your board. First by 'alcoho
Electronics Forum | Tue Sep 21 11:34:10 EDT 2004 | davef
Several things to check are: * Ask Multicore if their flux res and your conformal coat are compatible. Conformal coats and NC flux res are notorious for having compatibily issues. * Conformal coat a bare board to determine if there is there is enoug
Electronics Forum | Sat Apr 17 17:08:22 EDT 2004 | finepitch
Russ has a hint by saying "too long of a soak at too high of a temp or being in reflow for too long/hot". I think the board should stay in the oven for 3-4 minutes, spending 60-90 seconds of which during reflow. in order to stay in the oven for 3 m